Electroluminescence of In0.53Ga0.47As0.99N0.01/GaAs0.5Sb0.5 Type-II Quantum Well Light-Emitting Diodes Grown on InP Substrates by Molecular Beam Epitaxy
スポンサーリンク
概要
- 論文の詳細を見る
In0.53Ga0.47As0.99N0.01/GaAs0.5Sb0.5 type-II quantum well light-emitting diodes were grown on InP substrates by molecular beam epitaxy (MBE). The peak wavelength of the electroluminescence (EL) was as long as 2.66 μm at 10 K, which is much longer than that (2.08 μm) of In0.53Ga0.47As/GaAs0.5Sb0.5 type-II quantum well diodes on InP substrates. This is due to introduction of nitrogen into the InGaAs layers. A marked blue shift of the peak wavelength with increasing injection current was also observed, which is unique to the type-II quantum well structures.
- INSTITUTE OF PURE AND APPLIED PHYSICSの論文
- 2007-06-15
著者
-
KAWAMURA Yuichi
Frontier Science Innovation Center Osaka Prefecture University
-
INOUE Naohisa
Frontier Science Innovation Center Osaka Prefecture University
-
Kawamura Yuichi
Frontier Science Innovation Center, Osaka Prefecture University, Sakai 599-8570, Japan
関連論文
- Band-Gap Change in Ordered/Disordered GaAs_Sb_y Layers Grown on (001) and (111)B InP Substrates : Semiconductors
- Electroluminescence of In_Ga_As/GaAs_Sb_ Type-II Multiple Quantum Well Light-Emitting Diodes Grown on (111)B InP by Molecular Beam Epitaxy : Short Note
- Molecular Beam Epitaxial Growth and Characterization of GaAs_Sb_y Layers on (111)B InP Substrates
- MBE Growth and Characterization of InGaAsSbN Quantum Well Laser Diodes at 2μm Wavelength Region grown on InP Substrates
- InAsSbN Quantum Well Laser Diodes Operating at 2-μm-Wavelength Region Grown on InP Substrates
- 2.43 μm Light Emission of InGaAsSbN Quantum Well Diodes Grown on InP Substrates
- Emission Properties of InGaAsSbN Quantum Well Laser Diodes in 2 μm Wavelength Region Grown on InP Substrates
- Lasing Characteristics of InGaAsSbN Quantum Well Laser Diodes at 2-μm-Wavelength Region Grown on InP Substrates
- Electroluminescence of In0.53Ga0.47As0.99N0.01/GaAs0.5Sb0.5 Type-II Quantum Well Light-Emitting Diodes Grown on InP Substrates by Molecular Beam Epitaxy
- InAsSbN Quantum Well Laser Diodes Operating at 2-μm-Wavelength Region Grown on InP Substrates