Growth of ZnO Submicron Single-Crystalline Platelets, Wires, and Rods by Ultrasonic Spray Pyrolysis

概要

論文の詳細を見る
Submicron single crystals of ZnO were grown by spray pyrolysis: the mist of an aqueous solution was generated by ultrasonic agitation and then pyrolyzed on a heated glass substrate. Hexagonal platelets of ZnO 10–90 nm thick were obtained when ammonium acetate was incorporated into the precursor solution of zinc acetate. Single-crystalline wires and rods, which were 50–150 and 300–4000 nm thick respectively, were obtained when indium nitrate was co-incorporated into the solution as a metal catalyst. The crystallographic direction of wires and rods was parallel to one of the [0001], [$10\bar{1}0$], or [$11\bar{2}0$] axis of wurtzite. As substrate temperature increased, the aspect ratio of the crystal thus tended to decrease. Structural and compositional analyses of these crystals were performed by scanning electron microscopy, scanning ion microscopy, transmission electron microscopy and electron diffraction, X-ray diffraction, X-ray photoelectron spectrocopy, and energy dispersive X-ray spectroscopy.
Published by the Japan Society of Applied Physics through the Institute of Pure and Applied Physicsの論文
2007-01-15