高温保持後のSn-3.0Ag-0.5Cuはんだ接合部の疲労寿命評価

スポンサーリンク

概要

• 論文の詳細を見る

• The decrease in fatigue life of solder joints under the high temperature environment is a major problem in semiconductor packages for automotive applications. To clarify the mechanism of the fatigue-life decrease, we carried out the mechanical cyclic fatigue test of the Sn-3mass%Ag-0.5mass%Cu solder joint after high-temperature heat treatment. We studied a correlation between the heat treatment condition and the fatigue-life decrease. The method for estimating the fatigue life decrease from the heating history of heat cycle tests was also studied. The fatigue-life decrease of the solder joints after heat treatment was explained as the temporal change in the fatigue ductility coefficient of the Coffin-Manson's low, and the decreasing rate of fatigue life was converged within the range from 60 to 70%. We found that the fatigue-life decrease can be quantitatively estimated by using Arrhenius's low with the consideration of the heating temperature, hold time and the number of reliability target cycle of the heat cycle test.

著者

• 木本 良輔

  ルネサスエレクトロニクス

• 山本 健一

  ルネサスエレクトロニクス

• 河野 賢哉

  （株）日立製作所日立研究所

• 中 康弘

  （株）日立製作所日立研究所

• 谷江 尚史

  （株）日立製作所日立研究所

• 木本 良輔

  ルネサスエレクトロニクス（株）生産本部

関連論文

• PbフリーBGAはんだ接続部の衝撃耐性評価手法の確立 : (第1報)衝撃破断モードの基板ひずみ依存性の検討
• 半導体パッケージはんだ接続パッド引出し配線の疲労強度評価
• プリント基板配線の疲労強度評価手法の検討(技術OS3-2 微小材料強度評価,技術OS3 電子・情報機器と材料力学)
• 高信頼度BGAパッケージの構造設計
• 携帯機器用アンダーフィル実装試験片の強度評価
• PbフリーはんだBGA接続部の衝撃信頼性設計技術
• 衝撃曲げ試験によるBGAはんだ接続部の信頼性評価
• PbフリーはんだBGA接続部の衝撃信頼性設計技術
• PbフリーBGAはんだ接続部の衝撃耐性評価手法の確立（第2報） : はんだ接続部応力による衝撃耐性評価方法の検討
• J0601-4-1 高温熱処理後のSn3Ag0.5Cuはんだ接合部の疲労寿命評価([J0601-4]電子情報機器,電子デバイスの強度・信頼性評価と熱制御(4))
• PbフリーBGAはんだ接続部の衝撃耐性評価手法の確立 : (第2報)はんだ接続部応力による衝撃耐性評価方法の検討
• 高温保持後のSn-3.0Ag-0.5Cuはんだ接合部の疲労寿命評価
• J031031 高温劣化を考慮したSn3AgO.5Cuはんだ接合部の疲労寿命予測手法([J03103]電子情報機器,電子デバイスの強度・信頼性評価と熱制御(3))

もっと見る 閉じる

スポンサーリンク