BaTiO<SUB>3</SUB>のAgによる濡れ性への表面及び焼結密度の影響
スポンサーリンク
概要
- 論文の詳細を見る
Wetting properties of silver on Barium titanates (hereinafter, BT), on reduced BT (BaTi0<SUB>3-δ</SUB>) and on reoxidized BT (BaTiO<SUB>3-δ+x</SUB>) of reduced BT were studied using furnace with a telescope to measure contact angle in vacuum with elevating temperatures.<BR>The effects of surface roughness, sintered density, and the surface-oxidized conditions of the ceramics were examined and discussed. In addition, Ag containing borosilicate glass was also investigated to discuss the effects of the glass on the wetting properties on BT.<BR>As a result, the followings were clarified: The contact angles were reduced depending upon the sintered densities and surface roughness of ceramics, and oxidized layers on the ceramics affected to reduce the contact angles as well. The mechanism of adhesion of Ag on the ceramics was also discussed. The glass frits were thought to wet the ceramics regardless of sintered density and surface roughness.
- 社団法人 粉体粉末冶金協会の論文
著者
-
杉原 淳
湘南工科大学材料工学科
-
杉原 淳
湘南工科大学工学部マテリアル工学科
-
岡崎 清
湘南工科大学
-
寺島 良充
富士チタン工業(株)技術開発部
-
木佐森 克彦
富士チタン工業(株)技術開発部
-
杉原 淳
湘南工科大
関連論文
- SrTiO_3とCaTiO_3のTi-K XANESスペクトルにおける低エネルギーピークの起源
- 結晶のクラスターモデルによるXANESの解析 : ペロブスカイト型酸化物SrTiO_3 Ti Kスペクトル
- (Fe_,Ti_x)_2O_3の熱電特性と電子構造
- (Zn,Al)Oへの不純物添加による熱電性能の改善
- (Fe_Co_)Si_2への酸化物添加による熱電性能の改善
- Ca(Mn_,M_x)O_3の熱電特性 (M=Ta, Mo, Nb and Zn)
- 酸化物熱電半導体のゼーベック係数へ及ぼす電子構造と酸化物の役割
- 熱電変換材料への基礎的アプローチ
- 熱電材料の最近の開発状況と実用化動向
- ガラス相を利用したBaTiO_3の低温焼結