Bi-Pb-Sr-Ca-Cu-O系酸化物超伝導体の摩砕と一軸加圧成形の効果
スポンサーリンク
概要
- 論文の詳細を見る
The formation behavior of an amorphous phase in grinding and its recrystallization behavior by heat-treatment of seed-added powder were observed using a starting powder of the high Tc phase (2223 phase) superconductor having the composition Bi<SUB>1.5</SUB>Pb<SUB>0.4</SUB>Sr<SUB>2.0</SUB>Ca<SUB>2.0</SUB>Cu<SUB>3.2</SUB>O<SUB>y</SUB>. The effects of uniaxial press-forming in the opposed anvil type high pressure apparatus were investigated in relation to the properties of sintered compacts (bulk density, phase microstructure, critical temperature, etc.).<BR>Grinding the starting powder in agate mortar for 10-20 min initiated the formation of an amorphous phase and nearly completely amorphous phase was obtained by grinding for 100min. The heat treatment (at 850°C for 2h) of the amorphous powder which was added by 50 wt % starting powder as seeds, result-ed in the recrystallization to high Tc phase (2223 phase) in the presence of a trace of low Tc phase (2212 phase)<BR>Starting powder packed in a copper ring gasket was press-formed under high pressure (0.5-1.5 G P a) . A small amount of low Tc phase coexisted with high Tc phase in the specimen formed at 1.0 G Pa. The bulk density of the sintered compact prepared by the subsequent sintering at 850°C for 40h under one atmospheric pressure was 5.4g/em, and the critical onset and offset temperatures were 115K and 103K, respectively.
- 社団法人 粉体粉末冶金協会の論文
著者
-
伊藤 秀章
名古屋大学理工科学総合研究センター
-
伊藤 秀章
Division Of Environmental Research Ecotopia Science Institute Nagoya University
-
高田 潤
岡山大学 工学部
-
伊藤 秀章
名古屋大学工学部人工結晶研究施設
-
伊藤 秀章
名古屋大学
-
矢田 節男
金沢工業大学
-
中 重治
金沢工業大学
-
冨井 洋一
京都大学 工学部
-
高野 幹夫
京都大学 化学研究所
関連論文
- 傾斜組織化CVDによるダイヤモンド・コーティング工具の作製
- CVDダイヤモンド膜 -窒化ケイ素基板の密着性に及ぼすDLC中間層の効果
- 白金添加酸化チタン光触媒による芳香族炭化水素の芳香環ヒドロキシル化反応
- 340 Bi-2223 焼結体への 290MeV ^Ar 照射による超伝導特性の改善
- HF水溶液を用いた水熱処理による窒化ケイ素セラミックスの崩壊挙動
- 無機系・有機系産業廃棄物 から合成した多孔性材料の構造とガス吸着特性
- 環境・経済・社会・ヒューマンファクターにかかわる評価指標に関する研究 : 持続可能型エコトピア実現に資する指標
- CoB_10H_10の熱分解によるCoBの生成
- OMCVDによるZrO_2-MgO系薄膜の作製(イオン伝導性セラミックス)(導電性セラミックス)
- 難処理人工物の再資源化・無害化処理評価システム
- 無機系および有機系固体産業廃棄物の同時焼成処理により合成した多孔性吸着材料
- 光触媒的芳香環ヒドロキシル化反応における活性酸素種
- 白金添加酸化チタン光触媒による二置換アルカンの環化反応
- HF水溶液を用いた水熱処理による窒化ケイ素焼結体のリサイクル
- レスキュー・ナンバー(RN)によるWC-Co超硬合金リサイクルシステムの評価
- 超硬合金の各種雰囲気における熱分解とリサイクルの可能性
- 廃棄物の処理優先度および再資源化・無害化処理法評価の試み
- 1005 万年時計の機構解明 その3 : 動力部(S91-1 機械技術史・工学史(1),S91 機械技術史・工学史)
- 416 Mo-Ti合金における耐中性子照射特性の評価(W-Ti・Mo-Ti合金,一般セッション,第53期学術講演会)
- 415 多段内部窒化法を用いたW-Ti合金の組織制御(W-Ti・Mo-Ti合金,一般セッション,第53期学術講演会)
- 固体産業廃棄物を利用した活性炭分散セラミックス多孔体の作製と特性評価
- A12 Teaniolite配向薄膜中でのRhodamine 6Gの分子配向構造
- ニッケル基板上への窒化ホウ素膜の CVD
- ダイヤモンドの液相(反応)焼結におよぼす諸因子
- 水熱プロセスを利用した廃棄物からの高効率レアメタル回収技術の研究開発
- Phosphorus mineralization for resource recovery from wastewater using hydrothermal treatment(Aqueous Solution Science for Ceramic Processing II)
- A precipitation method for arsenite ion in aqueous solution as natural mineral by hydrothermal mineralization( Innovative Ceramic Materials and Technologies for Global Environmental Protection)
- In Situ Solid/Liquid Separation Effect for High-Yield Recovery of Boron and Fluorine from Aqueous Media Containing Borate or Fluoroborate Ions
- Detoxification of Antimonic Contaminated Water and Precipitation Recovery of Antimony by Mineralization under Hydrothermal Condition
- 使用済み電子写真用トナーキャリアの水熱処理による再生
- セラミックスのニュープロセスとナノテクノロジー : 4.セラミックスの再生技術
- Arsenic Recovery from Water Containing Arsenite Ions by Hydrothermal Mineralization
- A Novel Recovery Method for Treating Wastewater Containing Fluoride and Fluoroboric Acid
- 亜臨界水熱処理による超硬合金からのWO_3の回収(極限環境)
- 402 亜臨界水熱処理による超硬合金からの資源回収(高圧力フォーラム, 複合材料の成形・加工最前線)
- 回転粉体床CVDによるTiB_2-TiN二層被覆鉄粉体の調製
- 507 圧力下の熱水処理によるセラミック系廃棄物からの再焼結用粉末の回収(溶液・熱水処理と評価)(圧力による影響・処理・変化)(オーガナイスドセッション5)
- 無機・有機系固体産業廃棄物を利用した多孔性バルク体の合成とその機能評価
- 焼成発泡法によるCaTiO_3多孔質支持体の作製
- 窒化ケイ素基板への高密着性ダイヤモンド被覆
- B_6O粉末の高圧焼結と焼結体の性質(高圧力 : 固体の高圧物性, 反応, 実験技術)
- TiB_2-B_4C系複合焼結体の耐酸化特性
- 固相反応によるタンタルホウ化物粉末の合成と焼結
- 黒鉛のダイヤモンド化に及ぼすB_4CとTiC_xの添加効果
- 701 圧力をパラメータとする材料の合成と分解処理(極限環境フォーラム)
- タングステンホウ化物の合成におよぼす雰囲気処理の効果(粉体小特集)
- WBの合成と反応焼結(4.固相反応法)(新技術によるセラミックスの合成と評価(II))
- OMCVD法によるMnFe_2O_4膜の成長(2. 気相反応法)(新技術によるセラミックスの合成と評価(I))
- アセチルアセトナト錯体の熱分解CVDによる(Mn,Zn)Fe2O4膜の合成 (薄膜の形成と構造) -- (無機薄膜)
- VII. CVD超高硬度材料ダイヤモンド膜の微細構造
- 二段階マイクロ波プラズマCVDによるタングステン線へのダイヤモンドの核生成促進と密着性
- B-O系超硬物質の合成と焼結
- 粉体粒子へのCVDコーテイング
- 粉体工学講座-28-粒子特性制御工学-2-最近の微粒子制御技術-4-粒子集合体を固める技術-2-加圧焼結法
- 金属線への気相成長ダイヤモンドの微結晶コーティング
- マイクロ波プラズマ CVD による金属線へのダイヤモンドの析出分布と形態
- Bi-Pb-Sr-Ca-Cu-O系酸化物超伝導体の摩砕と一軸加圧成形の効果
- Bi系超伝導相へのPb置換効果
- 材料のライフサイクルと資源循環
- CVDダイヤモンドの核生成と成長機構 (1990年の化学-9-)
- YO1.5-CaO-CuO系の状態図
- 窒化ケイ素基板への高密着ダイヤモンドコ-ティング
- ダイヤモンドの液相(反応)焼結におよぼす諸因子
- CVDによるTiN被覆複合化粉体の調製
- 反応焼結によるcBN―ダイヤモンド複合焼結体の作製
- h-BNを出発原料とするc-BNの高圧焼結に及ぼす雰囲気前処理効果
- ダイヤモンドの反応焼結過程の観察
- 正方晶YBa2Cu3O6.76の構造および物性に与える酸素アニールの効果
- 湿式ボールミル法を用いたPLZTセラミックスからの鉛の回収
- 酸性溶媒を用いたボールミルによるPZTセラミックスからの鉛の回収
- セラミックス廃材からの有価および有害金属の資源回収
- A20 産業廃棄物を原料とする炭素-ゼオライト多孔性バルク体の作製と吸着特性
- Bi2+xSr2-xCu1+x/4Oz固溶体へのBa置換効果
- メスバウアー分光法によるBi3Fe5O12単結晶膜の磁気的性質の研究
- Bi (Pb)系酸化物超伝導体の焼結の臨界電流密度に及ぼす組成アルカリ土類元素の酸化物およびフッ化物の添加効果
- Bi系30Å相へのPb添加効果
- Bi-Pb-Sr-Ca-Cu-O系高Tc相の生成過程
- プラズマCVDで得られたAlN被覆黒鉛の耐酸化特性
- 超硬質セラミックス材料の創製と評価 : 第57回日本セラミックス協会学術賞受賞研究総説
- 廃葉物処理・管理の地域性とグローバル性のはざまで
- 学会がリストラの憂き目にあわないために
- 特集にあたって
- 固相反応による金属チタンまたは窒化チタンと非晶質ホウ素からの二ホウ化チタン粉末の合成
- Bi(Pb)-Sr-Ca-Cu-O系超伝導体の緻密化と臨界電流密度に及ぼす再加圧成形の効果
- Bi (Pb)系酸化物超伝導体の焼結挙動と臨界電流密度に及ぼすアルカリ土類酸化物の添加効果
- ホットプレスによるタングステンホウ化物焼結体の作製
- Bi1.8Pb0.4Sr2.0Ca2.0Cu3.2Oy超伝導焼結体の調製に及ぼす添加酸化物の効果
- Bi-Pb-Sr-Ca-Cu-O系超伝導相生成に及ぼすSb2O3の添加効果
- Bi-Sr-Ca-Cu-O系超伝導体の高Tc相生成に及ぼす"inert pair"元素酸化物の添加効果
- 金属添加酸化チタン光触媒によるアンモニア分解機構
- Bi,Pb-Sr-Ca-Cu-O系超伝導体の1軸加圧の圧力効果 (酸化物系超伝導物質と材料)
- Bi-Pb-Sr-Ca-Cu-O系高温相へのBa添加効果-2-Tcの上昇,生成の促進および固溶の確認 (酸化物系超伝導物質と材料)
- Tc=117KのBi-Pb-Sr-Ca-Cu-O系高温相 (酸化物系超伝導物質と材料)
- La2-xNdxCuO4+zの高酸素圧下での合成と性質 (酸化物系超伝導物質と材料)