Fe(III)系新規層状含水酸化物の合成とキャラクタリゼーション
スポンサーリンク
概要
- 論文の詳細を見る
A new layered iron hydroxide was synthesized by a wet chemical technique, by which aqueous ferrous sulfate solution was gradually oxidized by using sodium carbonate at 283∼333 K. Obtained yellowish precipitates identified by X-ray powder diffraction had a similar structure to the layered double hydroxides. The observed interlayer spacing was about d=0.74 nm. Electron micrographs showed that the particle had plate-like morphology. Electron diffraction pattern of the plate-like particles had hexagonal symmetry, when the electron beam was aligned normal to the planes. Mössbauer spectrum suggested that all iron ions were paramagnetic Fe3+ states with large quadrupole splittings at room temperature. These results show that the obtained new layered iron hydroxide cotains only Fe(III) ion species. Water vapor adsorption curves of the sample oxidized at 291 K showed high adsorption value (19 wt%) by unit weight.
著者
関連論文
- 22pPSA-1 元素置換イルメナイトFeM_xTi_O_3の構造と磁性(22pPSA 領域3ポスターセッション(酸化物・f電子系磁性・スピングラス・量子スピン・フラストレーション系・実験技術・磁性一般),領域3(磁性,磁気共鳴))
- Fe(III)系新規層状含水酸化物の合成とキャラクタリゼーション
- 27pYD-11 酸化鉄化合物/C60接合系におけるPN接合と光学特性(界面・分子デバイス3,領域7,分子性固体・有機導体)
- 20pPSA-51 Fe_2O_3-FeTiO_3固溶体薄膜の電気伝導特性(20pPSA 領域8ポスターセッション(低温II(Cu,Ru,Mn,Co酸化物など,磁束量子系)),領域8(強相関系:高温超伝導,強相関f電子系など))
- X線定在波法によるSrTiO3結晶のサイト選択的XPS測定
- 22aPS-73 光電子分光法による鉄-チタン酸化物の電子状態
- 31pXF-6 エピタキシャル FeTiO_3 薄膜の電子状態
- 27pXN-12 Ti Kβ X線輻射スペクトルにおける化学結合効果(原子・分子)(領域1)
- Fe (III) 系新規層状含水酸化物の合成とキャラクタリゼーション
- 290MeV/n^Ar照射によるBi-2223焼結体へのピニングセンター導入の試み