B_20_3を添加したGd-Fe共添加チタン酸バリウムの電気特性に及ぼす焼成雰囲気の影響

概要

論文の詳細を見る
Effect of firing atmosphere on the electrical properties of Gd-Fe-codoped BaTiO_3 ceramics added with B_2O_3 was studied by measuring their electrical resistivity, diffuse reflectance spectra and electron spin resonance (ESR) spectroscopy. The bulk density of the samples fired above 1300℃, except Fe-doped samples fired in air, was as high as 94% of the theoretical value. Semiconducting BaTiO_3 was obtained in the case of Fe-doped and un-doped samples fired in Ar at all range of firing temperature. The room temperature resistivity of the samples fired in Ar was lowered with increase in firing temperature. It was considered that the lowering of the resistivity was due to the grain growth with rise of temperature. The PTCR jump for Fe-doped samples fired in Ar was much larger in all range of firing temperature than that for Fe-undoped samples fired in Ar. This result indicated that Fe ions segregated in the grain boundary and acted as an acceptor.
社団法人日本材料学会の論文
2005-07-15