High-Pressure Phase Diagram and Variation of Elastic Moduli of Al-Li Alloy
スポンサーリンク
概要
- 論文の詳細を見る
The high-pressure phase diagram of an Al-rich Al-Li alloy at a 5.4-GPa pressure was investigated. To determine the equilibrium state under high-pressure and high-temperature conditions, the quenching method was applied and a phase analysis of the sample was performed using X-ray diffraction and microscopic observations. The resultant solid solubility of lithium in aluminum was subsequently increased up to 20 at% and the eutectic temperature increased to 800℃. Then the material properties (mainly elastic moduli) for supersaturated solid solutions treated under high pressure were also investigated. The shear modulus of the solid solutions increased at the rate of 0.28 GPa/at%Li ; in contrast, the bulk modulus decreased 0.52 GPa/at%Li.
- 一般社団法人日本機械学会の論文
- 1994-01-15
著者
-
MATSUMURO Akihito
Department of Mechanical Engineering, Nagoya University
-
Matsumuro Akihito
Department Of Mechanical Engineering Nagoya University
-
Matsumuro Akihito
Department Of Mechanical Engineering Aichi Institute Of Technology
-
Senoo Masafumi
Department Of Mechanical Engineering Faculty Of Engineering Nagoya University
-
Senoo Masafumi
Department Of Mechanical Engineering Mie University
-
Senoo Masafumi
Department Of Mechanical Engineering Faculty Of Engineering Mie University
-
Sakai Katsuhiko
Department of Mechanical Engineering, Nagoya University
-
Sakai Katsuhiko
Department Of Mechanical Engineering Nagoya University
関連論文
- Variation in Preferred Orientations of TiN Thin Films Prepared by Ion Beam Assisted Deposition
- Consideration of Deformation of TiN Thin Films with Preferred Orientation Prepared by Ion-Beam-Assisted Deposition
- Mechanical Properties of TiN Films with the Preferred Orientations by Nano-Indentation Method
- Structural Analysis of a Carbon Nitride Film Prepared by Ion-Beam-Assisted Deposition
- Influence of Deposition Temperatures on Bonding State and Microstructure of Carbon Nitride Thin Films Prepared by Ion-Beam-Assisted Deposition
- Aging Process in Supersaturated Al-10 at % Si Alloy Solution Treated at High Pressure
- TEM and HRTEM Observations of Microstructural Change of Silicon Single Crystal Scratched under Very Small Loading Forces by AFM
- High-Pressure Phase Diagram and Variation of Elastic Moduli of Al-Li Alloy
- Destruction and Recovery of Superconductivity in Bi-Pb-Sr-Ca-Cu-O Synthesized under High Pressure
- Ar Ion Effect on Mechanical Properties of Carbon Nitride Films Prepared by Ion-Beam-Assisted Deposition
- Precise Measurements of Lattice Compression of Al, Si and Al-Si Alloys by High Pressure X-Ray Diffractometry
- High Pressure Hot-Pressing of Y_1Ba_2Cu_3O_ Superconductor
- Calculations of Pressure-Volume Relations for Some Cubic Metals in Pseudopotential Method
- Lattice Compression of Al in Hydrostatic Environment Up to 70 kbar
- Solid Solubility of Si in Al under High Pressure
- Quenching Method for Vacancy Study of Metals under Very High Pressure
- High-Pressure Synthesis of a Bi-Pb-Sr-Ca-Cu-O Superconductor
- Microstructural Observation of Boron Nitride Films Synthesized by Ion Implantation