Solid Solubility of Si in Al under High Pressure

スポンサーリンク

概要

• 論文の詳細を見る

• By making use of a 15 mm cubic anvil apparatus, Al-Si alloys of Si-concentration up to 15 at % were studied at a pressure of 54 kbar. The liquidus, solidus and solvus of the Al-rich alloys were determined by means of the 4-probe electric resistance measurement. The solubility limit of Si in Al was extended beyond 15 at % at 54 kbar in comparison with 1.59 at % at 0 kbar. The resistivity of the alloy was increased by a solution of Si with a gradient of 0.5 μΩcm/at % up to 15 at % Si. The alloy quenched under high pressure was examined by X-ray diffractometry showing that Si was completely solid-dissolved in Al. The quenched alloy was much more hardened than the ordinary two-phase alloy at 0 kbar.

• 社団法人応用物理学会の論文
• 1976-05-05

著者

• Senoo Masafumi

  Department Of Mechanical Engineering Faculty Of Engineering Nagoya University

• Senoo Masafumi

  Department Of Mechanical Engineering Faculty Of Engineering Mie University

• Mii Hisao

  Department Of Mechanical Engineering Faculty Of Engineering Nagoya University

• FUJISHIRO Ikuya

  Department of Mechanical Engineering, Faculty of Engineering, Nagoya University

• Fujishiro Ikuya

  Department Of Mechanical Engineering Faculty Of Engineering Nagoya University

関連論文

• Aging Process in Supersaturated Al-10 at % Si Alloy Solution Treated at High Pressure
• High-Pressure Phase Diagram and Variation of Elastic Moduli of Al-Li Alloy
• Precise Measurements of Lattice Compression of Al, Si and Al-Si Alloys by High Pressure X-Ray Diffractometry
• Calculations of Pressure-Volume Relations for Some Cubic Metals in Pseudopotential Method
• Lattice Compression of Al in Hydrostatic Environment Up to 70 kbar
• Solid Solubility of Si in Al under High Pressure
• Quenching Method for Vacancy Study of Metals under Very High Pressure
• Microstructural Observation of Boron Nitride Films Synthesized by Ion Implantation