An Examination of the Notch Effect in Fatigue of Carbon Steels Based on Linear Notch Mechanics
スポンサーリンク
概要
- 論文の詳細を見る
Fatigue tests of 0.31% carbon steel specimens with a circumferential notch were made under a wide range of configuration parameters. As a result, it has been confirmed that linear notch mechanics (LNM) can be successfully applied to the evaluation of notch effects in fatigue. Master curves useful for the evaluation of notch effects in the fatigue of carbon steels were also obtained arranging the previously published data, based on LNM. Moreover, the fatigue limit of a specimen with a drilled hole was discussed using the above master curves.
- 一般社団法人日本機械学会の論文
- 1989-07-15
著者
-
NOGUCHI Hiroshi
Faculty of Engineering, Kyushu University
-
Nisitani Hironobu
Faculty Of Engineering Kyushu University
-
Uchihori Hisayuki
Faculty Of Engineering Kyushu University
-
Nakae Hiroshi
Faculty Of Engineering Kyushu University
-
Noguchi Hiroshi
Faculty Of Commerce University Of Marketing And Distribution Sciences
関連論文
- Loading-Frequency Effects on Fatigue Crack Growth Behavior of a Low Carbon Steel JIS S10C in Hydrogen Gas Environment
- Effect of Mean Stress on Fatigue Srength, Crack Strength and Notch Radius at Branch Point in Axial Fatigue of 7:3 Brass
- Crack Propagation in Low Cycle Fatigue of 7 : 3 Brass Specimens under Reversed Bending
- Observation of Local Deformation and Crack Initiation in High-Cycle Torsional Fatigue of Carbon Steel Plain Specimen by Electron Microscope
- Elastic Parameters Influencing Stress Fields in Multiphase Composite
- Analysis of Elastodynamic Problems Based on the Principle of Superposition : Extension of the Body Force Method to Elastodynamic Problems
- Effects of Hydrogen Gas Environment on Fatigue Strength at 107 cycles in Plain Specimen of Type 316L Stainless Steel
- Investigation of Local Hydrogen Distribution Around Fatigue Crack Tip of a Type 304 Stainless Steel with Secondary Ion Mass Spectrometry and Hydrogen Micro-Print Technique
- Quercetin 3-0-β-D-Glucopyranoside and Isorhamnetin 3-O-β-D-Glucopyranoside Formation from Quercetin by Cell Cultures of Ipomoea batatas and Crocus sativum(Biological Chemistry)
- Glucosylation of Quercetin by a Cell Suspension Culture of Vitis sp.(Biological Chemistry)
- Considerations of the Small-Crack Growth Law Based on COD : Low-Cycle Bending Fatigue Test of an Annealed 0.45%C Steel in the SEM
- Fatigue Damage of Heat-Treated 0.45%C Steel Smooth Specimens Under Two-Step Loading
- Statistical Property in the Initiation and Propagation of Microcracks of a Heat-Treated 0.45% C Steel
- Effect of Oil Viscosity on the Fatigue Limit of Drilled Specimens and the Small Crack Growth Law
- cDNA and Genomic DNA Clonings of Chalcone Synthase from Pueraria lobata
- Spirostanol and Furostanol Glycosides of Costus speciosus (KOENIG.) SM
- Low Pressure Hydrogen Gas Effect on Extremely Low Fatigue Crack Growth from Small Blind Holes of SUS304 and SUS316L
- Semi-Infinite Body with a Revolutional Pit Under Tension
- Semi-Infinite Body with a Semi-Ellipsoidal Pit under Tension
- Mode I and II Singular Stress Fields near a Corner of Jointed Dissimilar Materials
- Transverse Bending of Rectangular Plates with Single- or Double-Edge Cracks
- Anisotropy of Low-Cycle Torsional and Push-Pull Fatigue in a Rolled Steel
- Some Consideration on the Anisotropy of Fatigue Limit in a Rolled Steel Plate, Based on the Observation of Fatigue Process in Electropolished Specimens
- Anisotropy of the Fatigue Limit and of the Crack Propagation Property of a Rolled Steel Plate
- The Effect of Tensile Prestrain on the Fatigue Strength of Strength-Anisotropic Rolled Steel
- Effect of Heat Treatment on Anisotropy of Fatigue Strength of a Rolled Steel
- Influence of Mean Stress on Crack Closure Phenomenon and Fatigue Crack Propagation
- Strength Evaluation of Alumina Spray Coating : (4th Report, Consideration of Spray Structure Strength for Mechanical Stress)
- Investigation of Mechanism for Intergranular Fatigue Crack Propagation of Low Carbon Steel JIS S10C in Hydrogen Gas Environment
- Limits of Application for Two-Dimensional Elasticity Solutions in Plates Loaded in Tension and Out-of-Plane Bending
- Shear Characteristics of Hybrid Composites with Non-Woven Carbon Tissue
- Investigation of the Mechanism for Brittle-Striation Formation in Low Carbon Steel Fatigued in Hydrogen Gas : (Fractographic Observation on Fracture Processes Visualized by Controlling Load Sequence and Testing Environment)
- PD9 BIOSYNTHESIS OF FLAVONOIDS IN CELL SUSPENSION CULTURES OF PUERARIA LOBATA OHWI
- PD21 SECONDARY PRODUCTS FORMATION USING AGROBACTERIUM RHIZOGENES-TRANSFORMED "HAIRY ROOT" CULTURE AND ITS APPLICATION TO BIOSYNTHETIC STUDY
- Characteristics of Surface Crack Growth in Rotating Bending Tests of Age-hardened or Annealed Al-alloy
- 23083 Smeared crack models for shear analysis of RC members
- Fatigue Damage of Electropolished Carbon Steel Specimens with a Shallow Groove under Two Stress Levels
- Tension of an Infinite Elastic Body Having an Infinite Row of Spheroidal Cavities
- Rotary Bending Tests of Steel Specimens Having a Shallow but Sharp Circumferential Groove
- Effects of Size on the Fatigue Limit and the Branch Point in Rotary Bending Tests of Carbon Steel Specimens
- On the Tension of an Infinite Plate Containing an Infinite Row of Elliptic Holes
- Effect of Microstructure on the Characteristics of Small Fatigue Crack Growth in Dual-Phase Steels
- Minimum Fatigue Crack Length for the Application of Small-Crack Growth Law
- Fatigue Limit of Welded High Strength Steel and its Improvement Due to TIG Treatment : An Examination Based on Non-Propagating Phenomena of Crack
- Estimation of Crack Propagating Property by the Rotating Bending Fatigue Tests of Specimens with a Small Hole
- Analysis of Plasticity Induced Crack Closure by the Extended Body Force Method : Comparison of Various Analytical Results Based on Dugdale Model : Series A : Solid-Mechanics, Strength of Materials
- Improvement of the Accuracy in BEM or FEM Based on the Similarity of Stress Fields Near Notch Roots
- Singular Stress Field near a Corner of Jointed Dissimilar Materials under Antiplane Loads
- Analysis of Plasticity-Induced Crack Closure by the Extended Body Force Method : (Comparison of Various Analytical Results Based on Dugdale Hypothesis)
- Slip Deformation and Low-Cycle Fatigue Damage of an Aluminium Alloy
- Spirostanol and Furostanol Glycosides of Costus speciosus (KOENIG.) SM.
- Evaluation of Impact Strength due to Thermal Degradation for BGA-IC Package
- Strength Evaluation of Alumina Spray Coating : (5th Report, Consideration of the Strength in Sprayed Structure under Thermal Stress)
- Effect of Overstress on the Fatigue Behavior of a Heat-treated 0.54% C Steel under the Stress of Fatigue Limit
- Fracture Criterion of Notched Plates of FRP
- An Examination of the Notch Effect in Fatigue of Carbon Steels Based on Linear Notch Mechanics
- Torsional Fatigue and Bending Fatigue of Electropolished Low Carbon Steel Specimens
- Tensile Fracture Criterion of High Strength Steel Specimens with a Circumferential Notch : Solid-Mechanics, Strength of Materials
- Effect of Oil Environment on Characteristics of Fatigue Crack Growth of Age-Hardened Al-Alloy : Series A : Solid-Mechanics Strength of Materials
- Formation of Anthraquinones, Hydroanthracene and Flavonoid by the Callus Culture of Cassia torosa
- The Effect of Overstress on the Non-Propagating Crack Formed in a Specimen with a Small Hole : Series A : Solid-Mechanics, Strength of Materials
- Analysis of the Delaying Effects of Overloads on Fatigue Crack Propagation by the Body Force Method : Series A : Solid-Mechanics, Strength of Materials
- Correlation between the Existence of Fatigue Limit and Non-Propagating Micro-Crack
- A New Anthraquinone from Rubia tinctorum
- Bending or Torsional Fatigue of Notched Specimen with a Small Hole at the Notch Root
- THE RANKING OF TOTAL MEDALS WON BY EACH COUNTRY IN THE SYDNEY OLYMPICS BY USING DEA MODEL AFTER CLUSTERING
- Notch Effect in Low-Cycle Fatigue : 2nd Report : Effect of Stress Change and Mean Stress
- Comparison of Fatigue Processes in 0.45%C Steel Specimens Polished under Different Conditions
- Small Fatigue Crack Initiation and Propagation of Annealed 0.42% C Steel in Oil : Solid-Mechanics, Strength of Materials
- Fatigue Strength Characteristics of Non-Combustible Mg Alloy
- Identification of 10-Hydroxy-12Z-octadecenoic and 10-Hydroxy-12Z, 15Z-octadecadienoic Acids in Corn Silage
- Method of Approximate Calculation for Interference of Notch Effects and Its Application