Notch Effect in Low-Cycle Fatigue : 2nd Report : Effect of Stress Change and Mean Stress
スポンサーリンク
概要
- 論文の詳細を見る
The life prediction method developed in the 1st report for the low-cycle fatigue of notched specimens in completely reversed loading was applied to the low-cycle fatigue accompanied by (1) a change of stress amplitude and (2) the mean stress. The effectiveness of the method for these two cases is discussed with the measurement of the strain at notch root and the analysis by the finite element method. When a circumferentially notched specimen is subject to overloading, the strain range at notch root after overloading becomes smaller than the value without overloading. The strain ranges at notch root under the same stress amplitude and different mean stresses are nearly equal to each other and the crack initiation periods become nearly equal.
- 一般社団法人日本機械学会の論文
著者
-
Murakami Yukitaka
Department Of Mechanical Engineering Kyushu Institute Of Technology
-
Nisitani Hironobu
Faculty Of Engineering Kyushu University
-
KUSUMOTO Shoh
Hitachi Research Laboratory, Hitachi Ltd.
-
Kusumoto Shoh
Hitachi Research Laboratory Hitachi Ltd.
関連論文
- Effect of Mean Stress on Fatigue Srength, Crack Strength and Notch Radius at Branch Point in Axial Fatigue of 7:3 Brass
- Crack Propagation in Low Cycle Fatigue of 7 : 3 Brass Specimens under Reversed Bending
- Observation of Local Deformation and Crack Initiation in High-Cycle Torsional Fatigue of Carbon Steel Plain Specimen by Electron Microscope
- Fatigue Failure by In-line Flow-induced Vibration and Fatigue Life Evaluation
- Fatigue Failure by Flow-Induced Vibration : Effect of Initial Defect Size on Cumulative Fatigue Damage
- Elastic Parameters Influencing Stress Fields in Multiphase Composite
- Analysis of Elastodynamic Problems Based on the Principle of Superposition : Extension of the Body Force Method to Elastodynamic Problems
- Considerations of the Small-Crack Growth Law Based on COD : Low-Cycle Bending Fatigue Test of an Annealed 0.45%C Steel in the SEM
- Fatigue Damage of Heat-Treated 0.45%C Steel Smooth Specimens Under Two-Step Loading
- Statistical Property in the Initiation and Propagation of Microcracks of a Heat-Treated 0.45% C Steel
- Effect of Oil Viscosity on the Fatigue Limit of Drilled Specimens and the Small Crack Growth Law
- Fatigue and Tribological Properties of Materials for Hydrogen Service
- Semi-Infinite Body with a Revolutional Pit Under Tension
- Semi-Infinite Body with a Semi-Ellipsoidal Pit under Tension
- Mode I and II Singular Stress Fields near a Corner of Jointed Dissimilar Materials
- P-01-A Relation between high molecular weight proteins and surface layer in Bacteroides forsythus(THE JOINT MEETING OF THE 44TH ANNUAL MEETING OF THE JAPAN SOCIETY OF HISTOCHEMISTRY AND CYTOCHEMISTRY AND THE 35TH ANNUAL MEETING OF THE CLINICAL ELECTRON MI
- Localization of Major, High Molecular Weight Proteins in Bacteroides forsythus
- Transverse Bending of Rectangular Plates with Single- or Double-Edge Cracks
- Anisotropy of Low-Cycle Torsional and Push-Pull Fatigue in a Rolled Steel
- Some Consideration on the Anisotropy of Fatigue Limit in a Rolled Steel Plate, Based on the Observation of Fatigue Process in Electropolished Specimens
- Anisotropy of the Fatigue Limit and of the Crack Propagation Property of a Rolled Steel Plate
- The Effect of Tensile Prestrain on the Fatigue Strength of Strength-Anisotropic Rolled Steel
- Effect of Heat Treatment on Anisotropy of Fatigue Strength of a Rolled Steel
- Fatigue Strength of Ti-6Al-4V Alloys Containing Small Artificial Defects
- Integration Technology of Machine Systems for Hydrogen Utilization
- Influence of Mean Stress on Crack Closure Phenomenon and Fatigue Crack Propagation
- Analysis of Major Virulence Factors in Porphyromonas gingivalis under Various Culture Temperatures Using Specific Antibodies
- Characteristics of Surface Crack Growth in Rotating Bending Tests of Age-hardened or Annealed Al-alloy
- Fatigue Damage of Electropolished Carbon Steel Specimens with a Shallow Groove under Two Stress Levels
- Tension of an Infinite Elastic Body Having an Infinite Row of Spheroidal Cavities
- Rotary Bending Tests of Steel Specimens Having a Shallow but Sharp Circumferential Groove
- Effects of Size on the Fatigue Limit and the Branch Point in Rotary Bending Tests of Carbon Steel Specimens
- On the Tension of an Infinite Plate Containing an Infinite Row of Elliptic Holes
- Effect of Microstructure on the Characteristics of Small Fatigue Crack Growth in Dual-Phase Steels
- Minimum Fatigue Crack Length for the Application of Small-Crack Growth Law
- Fatigue Limit of Welded High Strength Steel and its Improvement Due to TIG Treatment : An Examination Based on Non-Propagating Phenomena of Crack
- Estimation of Crack Propagating Property by the Rotating Bending Fatigue Tests of Specimens with a Small Hole
- Analysis of Plasticity Induced Crack Closure by the Extended Body Force Method : Comparison of Various Analytical Results Based on Dugdale Model : Series A : Solid-Mechanics, Strength of Materials
- Effects of Small Defects on Fatigue Strength of T1-6A1-4V Alloy(Fatigue 1)
- Improvement of the Accuracy in BEM or FEM Based on the Similarity of Stress Fields Near Notch Roots
- Singular Stress Field near a Corner of Jointed Dissimilar Materials under Antiplane Loads
- Analysis of Plasticity-Induced Crack Closure by the Extended Body Force Method : (Comparison of Various Analytical Results Based on Dugdale Hypothesis)
- Slip Deformation and Low-Cycle Fatigue Damage of an Aluminium Alloy
- DURABILITY TEST AND DAMAGE EVALUATION OF HARD DISKS
- Effect of Overstress on the Fatigue Behavior of a Heat-treated 0.54% C Steel under the Stress of Fatigue Limit
- Fracture Criterion of Notched Plates of FRP
- An Examination of the Notch Effect in Fatigue of Carbon Steels Based on Linear Notch Mechanics
- Torsional Fatigue and Bending Fatigue of Electropolished Low Carbon Steel Specimens
- Tensile Fracture Criterion of High Strength Steel Specimens with a Circumferential Notch : Solid-Mechanics, Strength of Materials
- Effect of Oil Environment on Characteristics of Fatigue Crack Growth of Age-Hardened Al-Alloy : Series A : Solid-Mechanics Strength of Materials
- The Effect of Overstress on the Non-Propagating Crack Formed in a Specimen with a Small Hole : Series A : Solid-Mechanics, Strength of Materials
- Analysis of the Delaying Effects of Overloads on Fatigue Crack Propagation by the Body Force Method : Series A : Solid-Mechanics, Strength of Materials
- Stress Singularity at the Corner Point of 3-D Surface Crack under Mode II Loading(Stress Analysis)
- Correlation between the Existence of Fatigue Limit and Non-Propagating Micro-Crack
- Bending or Torsional Fatigue of Notched Specimen with a Small Hole at the Notch Root
- A Simple Procedure for the Accurate Determination of Stress Ihtensity Factors By Finite Element Method
- Notch Effect in Low-Cycle Fatigue : 2nd Report : Effect of Stress Change and Mean Stress
- Effects of Small Defects and Nonmetallic Inclusions on the Fatigue Strength of Metals
- Comparison of Fatigue Processes in 0.45%C Steel Specimens Polished under Different Conditions
- Small Fatigue Crack Initiation and Propagation of Annealed 0.42% C Steel in Oil : Solid-Mechanics, Strength of Materials
- Method of Approximate Calculation for Interference of Notch Effects and Its Application