Characteristics of Surface Crack Growth in Rotating Bending Tests of Age-hardened or Annealed Al-alloy
スポンサーリンク
概要
- 論文の詳細を見る
Rotating bending fatigue tests were carried out to evaluate the characteristics of surface crack growth in an age-hardened Al-alloy and an annealed Al-alloy The main results obtained are as follows : (1) The rack growth rate in an annealed Al-alloy is expressed by the following equation. dl/dN = Cσ^n 1 (C,n : material constants ) The number of cycles to failure of a plain specimen can be estimated by this equation. (2) In case of an age-hardened Al-alloy, a surface crack propagates rapidly along a slip band when the crack is short, and then the crack propagates zigzag, in that time the increase in the crack growth rate is low.
- 一般社団法人日本機械学会の論文
著者
-
Kawagoishi Norio
Faculty Of Engineering Kagoshima University
-
Kawagoishi Norio
Faculty Of Engineering Kagosima University
-
Nisitani Hironobu
Faculty Of Engineering Kyushu University
関連論文
- Effect of Mean Stress on Fatigue Srength, Crack Strength and Notch Radius at Branch Point in Axial Fatigue of 7:3 Brass
- Crack Propagation in Low Cycle Fatigue of 7 : 3 Brass Specimens under Reversed Bending
- Observation of Local Deformation and Crack Initiation in High-Cycle Torsional Fatigue of Carbon Steel Plain Specimen by Electron Microscope
- Generation Mechanism of Work Hardened Surface Layer in Metal Cutting : Study of Mechanical Factors Acting on Depth of Work Hardened Surface Layer Using Calculation Model
- A Study on Control for the Diminution of the Size of Burr in Metal Cutting
- Elastic Parameters Influencing Stress Fields in Multiphase Composite
- Analysis of Elastodynamic Problems Based on the Principle of Superposition : Extension of the Body Force Method to Elastodynamic Problems
- Considerations of the Small-Crack Growth Law Based on COD : Low-Cycle Bending Fatigue Test of an Annealed 0.45%C Steel in the SEM
- Fatigue Damage of Heat-Treated 0.45%C Steel Smooth Specimens Under Two-Step Loading
- Statistical Property in the Initiation and Propagation of Microcracks of a Heat-Treated 0.45% C Steel
- Effect of Oil Viscosity on the Fatigue Limit of Drilled Specimens and the Small Crack Growth Law
- Semi-Infinite Body with a Revolutional Pit Under Tension
- Semi-Infinite Body with a Semi-Ellipsoidal Pit under Tension
- Mode I and II Singular Stress Fields near a Corner of Jointed Dissimilar Materials
- Transverse Bending of Rectangular Plates with Single- or Double-Edge Cracks
- Anisotropy of Low-Cycle Torsional and Push-Pull Fatigue in a Rolled Steel
- Some Consideration on the Anisotropy of Fatigue Limit in a Rolled Steel Plate, Based on the Observation of Fatigue Process in Electropolished Specimens
- Anisotropy of the Fatigue Limit and of the Crack Propagation Property of a Rolled Steel Plate
- The Effect of Tensile Prestrain on the Fatigue Strength of Strength-Anisotropic Rolled Steel
- Effect of Heat Treatment on Anisotropy of Fatigue Strength of a Rolled Steel
- Effect of Shot Peening on Fatigue Strength of 18% Ni Maraging Steel
- Influence of Mean Stress on Crack Closure Phenomenon and Fatigue Crack Propagation
- Characteristics of Surface Crack Growth in Rotating Bending Tests of Age-hardened or Annealed Al-alloy
- Fatigue Damage of Electropolished Carbon Steel Specimens with a Shallow Groove under Two Stress Levels
- Tension of an Infinite Elastic Body Having an Infinite Row of Spheroidal Cavities
- Rotary Bending Tests of Steel Specimens Having a Shallow but Sharp Circumferential Groove
- Effects of Size on the Fatigue Limit and the Branch Point in Rotary Bending Tests of Carbon Steel Specimens
- On the Tension of an Infinite Plate Containing an Infinite Row of Elliptic Holes
- Effect of Microstructure on the Characteristics of Small Fatigue Crack Growth in Dual-Phase Steels
- Minimum Fatigue Crack Length for the Application of Small-Crack Growth Law
- Fatigue Limit of Welded High Strength Steel and its Improvement Due to TIG Treatment : An Examination Based on Non-Propagating Phenomena of Crack
- Fatigue Crack Growth Laws in Small and Large Cracks and Their Physical Background
- Estimation of Crack Propagating Property by the Rotating Bending Fatigue Tests of Specimens with a Small Hole
- Analysis of Plasticity Induced Crack Closure by the Extended Body Force Method : Comparison of Various Analytical Results Based on Dugdale Model : Series A : Solid-Mechanics, Strength of Materials
- Improvement of the Accuracy in BEM or FEM Based on the Similarity of Stress Fields Near Notch Roots
- Singular Stress Field near a Corner of Jointed Dissimilar Materials under Antiplane Loads
- Analysis of Plasticity-Induced Crack Closure by the Extended Body Force Method : (Comparison of Various Analytical Results Based on Dugdale Hypothesis)
- Slip Deformation and Low-Cycle Fatigue Damage of an Aluminium Alloy
- Effect of Overstress on the Fatigue Behavior of a Heat-treated 0.54% C Steel under the Stress of Fatigue Limit
- Fracture Criterion of Notched Plates of FRP
- An Examination of the Notch Effect in Fatigue of Carbon Steels Based on Linear Notch Mechanics
- Torsional Fatigue and Bending Fatigue of Electropolished Low Carbon Steel Specimens
- Tensile Fracture Criterion of High Strength Steel Specimens with a Circumferential Notch : Solid-Mechanics, Strength of Materials
- Effect of Oil Environment on Characteristics of Fatigue Crack Growth of Age-Hardened Al-Alloy : Series A : Solid-Mechanics Strength of Materials
- The Effect of Overstress on the Non-Propagating Crack Formed in a Specimen with a Small Hole : Series A : Solid-Mechanics, Strength of Materials
- Analysis of the Delaying Effects of Overloads on Fatigue Crack Propagation by the Body Force Method : Series A : Solid-Mechanics, Strength of Materials
- Correlation between the Existence of Fatigue Limit and Non-Propagating Micro-Crack
- Bending or Torsional Fatigue of Notched Specimen with a Small Hole at the Notch Root
- Notch Effect in Low-Cycle Fatigue : 2nd Report : Effect of Stress Change and Mean Stress
- Comparison of Fatigue Processes in 0.45%C Steel Specimens Polished under Different Conditions
- Small Fatigue Crack Initiation and Propagation of Annealed 0.42% C Steel in Oil : Solid-Mechanics, Strength of Materials
- Method of Approximate Calculation for Interference of Notch Effects and Its Application