Low Pressure Hydrogen Gas Effect on Extremely Low Fatigue Crack Growth from Small Blind Holes of SUS304 and SUS316L
スポンサーリンク
概要
- 論文の詳細を見る
In order to investigate the hydrogen gas effect on the fatigue limits of austenitic stainless steels, SUS304 and SUS316L, with small twin blind holes, metal fatigue tests were carried out in low pressure hydrogen gas, in air and in inert gases; i.e., argon or nitrogen. The fatigue limit of SUS304 is defined as the crack propagation limit not only in air, but also in hydrogen and nitrogen. The fatigue limit of SUS304 in hydrogen gas is slightly higher than that in air. The extremely low Fatigue Crack Growth Rates (FCGR) of not only SUS304, but also SUS316L in hydrogen gas is lower than that in argon gas in the FCGR region of less than 10-9m/cycle. This seems to be due to the plasticity-induced crack closure, and supports the higher fatigue limit in hydrogen.
著者
-
NISHIKAWA Hide-aki
Graduate School of Engineering, Kyushu University
-
Oda Yasuji
Faculty Of Engineering Kyushu University
-
Noguchi Hiroshi
Faculty Of Commerce University Of Marketing And Distribution Sciences
-
MATSUNO Hiroyuki
Graduate School of Engineering, Kyushu University
関連論文
- Loading-Frequency Effects on Fatigue Crack Growth Behavior of a Low Carbon Steel JIS S10C in Hydrogen Gas Environment
- Analysis of Elastodynamic Problems Based on the Principle of Superposition : Extension of the Body Force Method to Elastodynamic Problems
- Effects of Hydrogen Gas Environment on Fatigue Strength at 107 cycles in Plain Specimen of Type 316L Stainless Steel
- Investigation of Local Hydrogen Distribution Around Fatigue Crack Tip of a Type 304 Stainless Steel with Secondary Ion Mass Spectrometry and Hydrogen Micro-Print Technique
- Quercetin 3-0-β-D-Glucopyranoside and Isorhamnetin 3-O-β-D-Glucopyranoside Formation from Quercetin by Cell Cultures of Ipomoea batatas and Crocus sativum(Biological Chemistry)
- Glucosylation of Quercetin by a Cell Suspension Culture of Vitis sp.(Biological Chemistry)
- Considerations of the Small-Crack Growth Law Based on COD : Low-Cycle Bending Fatigue Test of an Annealed 0.45%C Steel in the SEM
- cDNA and Genomic DNA Clonings of Chalcone Synthase from Pueraria lobata
- Low Pressure Hydrogen Gas Effect on Extremely Low Fatigue Crack Growth from Small Blind Holes of SUS304 and SUS316L
- Semi-Infinite Body with a Revolutional Pit Under Tension
- Semi-Infinite Body with a Semi-Ellipsoidal Pit under Tension
- Strength Evaluation of Alumina Spray Coating : (4th Report, Consideration of Spray Structure Strength for Mechanical Stress)
- Investigation of Mechanism for Intergranular Fatigue Crack Propagation of Low Carbon Steel JIS S10C in Hydrogen Gas Environment
- Limits of Application for Two-Dimensional Elasticity Solutions in Plates Loaded in Tension and Out-of-Plane Bending
- Shear Characteristics of Hybrid Composites with Non-Woven Carbon Tissue
- Investigation of the Mechanism for Brittle-Striation Formation in Low Carbon Steel Fatigued in Hydrogen Gas : (Fractographic Observation on Fracture Processes Visualized by Controlling Load Sequence and Testing Environment)
- PD9 BIOSYNTHESIS OF FLAVONOIDS IN CELL SUSPENSION CULTURES OF PUERARIA LOBATA OHWI
- PD21 SECONDARY PRODUCTS FORMATION USING AGROBACTERIUM RHIZOGENES-TRANSFORMED "HAIRY ROOT" CULTURE AND ITS APPLICATION TO BIOSYNTHETIC STUDY
- 23083 Smeared crack models for shear analysis of RC members
- Improvement of the Accuracy in BEM or FEM Based on the Similarity of Stress Fields Near Notch Roots
- Spirostanol and Furostanol Glycosides of Costus speciosus (KOENIG.) SM.
- Evaluation of Impact Strength due to Thermal Degradation for BGA-IC Package
- Strength Evaluation of Alumina Spray Coating : (5th Report, Consideration of the Strength in Sprayed Structure under Thermal Stress)
- An Examination of the Notch Effect in Fatigue of Carbon Steels Based on Linear Notch Mechanics
- Tensile Fracture Criterion of High Strength Steel Specimens with a Circumferential Notch : Solid-Mechanics, Strength of Materials
- Formation of Anthraquinones, Hydroanthracene and Flavonoid by the Callus Culture of Cassia torosa
- A New Anthraquinone from Rubia tinctorum
- THE RANKING OF TOTAL MEDALS WON BY EACH COUNTRY IN THE SYDNEY OLYMPICS BY USING DEA MODEL AFTER CLUSTERING
- Fatigue Strength Characteristics of Non-Combustible Mg Alloy
- Identification of 10-Hydroxy-12Z-octadecenoic and 10-Hydroxy-12Z, 15Z-octadecadienoic Acids in Corn Silage