ホットプレス法により作製したLaPO_4被覆アルミナ繊維/アルミナマトリックス複合材の高温機械的性質

概要

論文の詳細を見る
High-temperature strength, fracture behavior and microstructure were observed for monazite-coated alumina fiber-reinforced alumina matrix composites hot-pressed at 1200-1300℃. The composites with 27-41 vol% alumina fiber showed no significant change in strength at 25-1100℃. However, the strength of the composites decreased markedly at a test temperature higher than 1100℃. The composites hot-pressed at a temperature lower than 1250℃ fractured in a pseudoductile manner in the test temperature range from 25℃ to 1100℃. Young's modulus of the elastic region decreased with increasing test temperature. These composites showed larger deformation at a test temperature above 1100℃. On the other hand, the composites hot-pressed at more than 1250℃ fractured in a brittle manner at 25℃-1200℃ of test temperature. The fracture energy of the composite increased with increasing test temperature and decreased with sintering temperature.
2004-12-01