マグネシア添加SiCセラミックスの焼結とその熱的・機械的・電気的特性
スポンサーリンク
概要
- 論文の詳細を見る
The suitability of MgO as a densification additive for SiC was investigated. Dense and fine-grained SiC ceramics could be obtained by hot-pressing at 1900℃ with addition>1 mass% (and up to 29 mass%) of MgO. X-ray diffraction (XRD) analysis of the SiC ceramics showed little reaction between SiC and MgO except for formation of small amount of Mg_2SiO_4, which indicated the presence of a liquid phase at high temperature. XRD analysis also showsd the transformation from 3C-SiC to 4H-SiC during hot-pressing. The grain sizes of the SiC sintered with 2-29 mass% MgO were almost the same and in the range of 100-300 nm. Mechanical properties, thermal conductivity and electrical properties of these ceramics were measured and discussed in relation to their microstructure.
- 2001-03-01
著者
-
安田 公一
東京工業大学
-
井関 孝善
東京工業大学大学院理工学研究科材料工学専攻
-
井関 孝善
東京工業大学
-
矢野 豊彦
東京工業大学原子炉工学研究所
-
松尾 陽太郎
東京工業大学大学院
-
松尾 陽太郎
東工大院
-
宮崎 広行
東京工業大学工学部無機材料工学科
-
井関 孝善
東工大原子炉研
-
箱守 明
東京工業大学大学院理工学研究科材料工学専攻
-
矢野 豊彦
東京工業大学工学学部無機材料工学科
-
矢野 豊彦
東京工業大
-
安田 公一
東京工業大学大学院材料工学専攻
-
宮崎 広行
東京工業大学大学院理工学研究科材料工学専攻:北海度工業技術研究所極限環境材料部微小重力工学研究室
-
松尾 陽太郎
東京工業大学
関連論文
- TZPセラミックスの超塑性変形における粒子流跡線のブラウン運動に基づく解析(M&P2009機械材料・材料加工部門技術講演会)
- SiCt常圧焼結体における板状粒子の多形
- メチルトリエトキシシランと種々の金属アルコキシドから作製した有機無機ハイブリッドコーティング膜のオイルへの塗れ性と摺動特性(有機-無機変換プロセス)
- 遷移金属を含有するポリメチルシルセスキオキサン系ハイブリッド及びシリコンオキシカーバイドセラミックスの合成 : コーティング膜及び独立膜の作製
- 熱衝撃および機械的応力を受けたアルミナー黒鉛質耐火物の超音波パルスエコー法による損傷評価
- 連鋳用耐火物の熱スポール破壊の統計解析
- 連鋳用耐火物の熱衝撃破壊におけるき裂の観察
- 連鋳用耐火物の熱衝撃破壊とその統計論的解析
- 焼結助剤の異なるSiC焼結体とAg-Cu-Ti合金との接合界面構造
- TZPセラミックスの超塑性変形における粒子流跡線のブラウン運動に基づく解析