連続鋳造浸漬ノズルの介在物付着に及ぼす耐火物材質の影響と介在物付着モデルに基づく考察

概要

論文の詳細を見る
New immersion nozzle materials preventing inclusion deposition have been investigated by laboratory scale test. A new mathematical model has been proposed to explain the behavior of inclusion in the turbulent boundary layer near the nozzle and deposition rate of inclusions in the molten steel has been numerically evaluated. (1) The quantity of deposited inclusions has drastically decreased in the materials composed with high Al_2O_3 in comparison with Al_2O_3-C one. There is no deposition of inclusions on the material composed with pure Al_2O_3 (Sapphire). (2) About 30% of the inclusions less than 20μm in diameter reach at laminar sublayer and they are forced to move onto the refractory wall due to the interfacial tension gradient between inclusions and molten steel, formed by concentration gradient of silicon etc. in molten steel. (3) Deposition rate of inclusions in the molten steel was evaluated to be 0.75μm/s (1.35mm thickness in 30 min) which is almost equal to the experimental results.
社団法人日本鉄鋼協会の論文