Electric-field-induced strain for (Bi1/2Na1/2)TiO3-based lead-free multilayer actuator
スポンサーリンク
概要
- 論文の詳細を見る
Multilayer prototype actuators were demonstrated using (Bi1/2Na1/2)TiO3 [BNT]-based ceramics as active layers and Pt as internal electrodes. One of the BNT-based solid solutions, 0.68(Bi1/2Na1/2)TiO3–0.04(Bi1/2Li1/2)TiO3–0.28(Bi1/2K1/2)TiO3 (BNLKT4–28) has been selected as the an active layer and it showed a relatively large piezoelectric strain constant d33 of 130 pC/N and a high depolarization temperature Td of 226°C. The total number of layers was 10 and the active layer thickness was 125 µm for the sintered body. The final compact dimensions were approximately 5 × 5 × 2 mm3. From the SEM observation, there were no apparent delaminations around the interface between Pt electrodes and active BNLKT layers. The large electric-field-induced strain at 70 kV/cm was 0.17% and the longitudinal dynamic displacement at the same electric field was 2.1 µm.
著者
-
竹中 正
東京理科大学理工学部
-
TAKENAKA Tadashi
Faculty of Science and Technology Tokyo University of Science
-
Nagata Hajime
Department of Electrical Engineering, Faculty of Science and Technology, Tokyo University of Science
-
Hiruma Yuji
Department of Electrical Engineering, Faculty of Science and Technology, Tokyo University of Science
-
Takenaka Tadashi
Department of Electrical Engineering, Faculty of Science and Technology, Tokyo University of Science
-
Takenaka Tadashi
Department Of Electrical Engineering Science University Of Tokyo
-
Takenaka Tadashi
Depart. Elect. Eng. Fac. Science And Technology Science University Of Tokyo
-
Nagata Hajime
Department Of Clinical Laboratory Tonami General Hospital
-
Hiruma Yuji
Department Of Electrical Engineering Faculty Of Science And Technology Tokyo University Of Science
関連論文
- 超音波圧電デバイスの無鉛材料化(環境問題と音響技術)
- 非鉛系圧電セラミックスの研究開発動向と将来展望
- Direct Crystallization and Characterization of Bi_3TiTaO_9 Thin Films Prepared by Metalorganic Chemical Vapor Deposition
- PLD法により作製された酸化亜鉛薄膜中の酸素拡散
- 圧電体の電気機械結合係数測定法に試料形状が与える影響 : 電極面が傾いている場合
- 圧電体の電気機械結合係数測定法に試料形状が与える影響
- 変調構造酸化亜鉛とその電気伝導性
- Electric-field-induced strain for (Bi1/2Na1/2)TiO3-based lead-free multilayer actuator
- 高温圧電センサ応用にむけた強誘電体セラミックスの開発 (特集 高温電子セラミックス)
- 26aYJ-5 Bi_Na_TiO_3のLi置換効果(誘電体(ペロブスカイト),領域10,誘電体,格子欠陥,X線・粒子線,フォノン物性)
- 非鉛系圧電セラミックスの最近の研究開発状況 (特集 環境とセラミックス)
- 非鉛系圧電セラミックスの研究開発状況とその課題 (特集 非鉛系圧電材料(1))
- 電子セラミックスの最先端研究動向と将来展望
- 1P1-18 KNbO_3系強誘電体セラミックスのシェアモード圧電特性(ポスターセッション)
- 1P1-14 (Bi_Na_)TiO_3-(Bi_K_)TiO_3-BaTiO_3三成分系の相関系と電気的諸特性(ポスターセッション)
- 1P1-9 粒子配向型(Bi_K_)TiO_3-BaTiO_3 セラミックスの電気的諸特性(ポスターセッション)
- 2-01P-04 粒子配向型(Bi_K_TiO_3-BaTiO_3系セラミックスの作製とその圧電的諸特性(ポスターセッション 2)
- 1-INV 非鉛系圧電セラミックスの研究開発状況と課題(招待講演 1)
- 高い機械的品質係数を持つビスマス層状構造強誘電体セラミックス
- P3-18 (Bi_Na_)TiO_3-(Bi_K_)TiO_3系非鉛圧電セラミックスの電気的諸特性(ポスターセッション3(概要講演))
- P3-13 BiおよびMn同時添加によるKNbO_3強誘電体セラミックスの圧電的性質(ポスターセッション3(概要講演))
- 非鉛系圧電材料の研究開発動向
- P1-28 (Bi_Na_)TiO_3-(Bi_K_)TiO_3-BaTiO_3三成分系非鉛圧電セラミックス(ポスターセッション1(概要講演))
- セラミックスの電磁気的・光学的性質 : 誘電的性質誘電性
- Number of Dielectric Layers Dependence of Dielectric Properties and Residual Stress of Multilayer Ceramic Capacitors with Ni Electrodes
- 1L06 環境を配慮した非鉛系圧電材料の現状
- IFFF2002(ISAF XIII/ISIF XIV/FMA XIX)
- PL測定による酸化亜鉛ヘテロ構造薄膜評価(セラミックスインテグレーション)
- ビスマス層状構造強誘電体セラミックスの電気的特性に及ぼす粒子配向の効果
- 環境に優しい非鉛系圧電セラミックス (特集 21世紀に開花するニューマテリアルとそのテクノロジーへの招待--東京理科大学における先端材料研究)
- 3F08 粒子配向型ビスマス層状構造強誘電体の圧電異方性
- 3A14 (Bi_Na_)TiO_3 セラミックスの微細構造に及ぼす添加物効果
- 第3回アジア強誘電体会議(AMF-3)
- ビスマス層状構造強誘電体セラミックスの圧電的諸特性
- ElectroCERAMICS VII
- 非鉛系圧電材料の研究動向--非鉛系圧電セラミックスの実用化に向けて (特集:環境にやさしい非鉛系圧電材料--セラミックスを中心として)
- 1D03 ビスマス層状構造強誘電体 Sr_Bi_Ta_xO_ の巨大異方性
- PA-13 斜め櫛型電極屈曲変位型圧電アクチュエータ
- 第2回強誘電体アジア会議(AMF-2)
- ISAF XI '98/ECAPD IV '98/Electroceramics VI '98
- 第8回日米誘電体・圧電体セラミックスセミナー
- 第9回強誘電体国際会議 (IMF-9)
- Lead-Free Piezoelectric Ceramics of (Bi_Na_)TiO_3-1/2(Bi_2O_3・Sc2_O_3) System
- PLZTセラミックスとAg電極間の反応及び拡散
- 焦電特性測定法の標準化のための調査研究
- Possibility of New Mixed Bismuth Layer-Structured Ferroelectrics
- 第7回日米誘電体圧電体セラミックスセミナ
- 西安会議(AMF-1 & ICECM-ICSA '95)
- MOCVD法によるPZT系強誘電体薄膜の作製とその評価(2)
- MOCVD法によるPZT系強誘電体薄膜の作製とその評価
- 第3回ヨーロッパセラミックス会議
- データベース利用 - 私の場合 -
- 第2回極性誘電体ヨーロッパ会議 (ECAPD-2)
- 3A22 MOCVD 法による PZT 系薄膜の作製とその評価
- ISAF XI '98/ECAPD IV '98/Electroceramics VI '98
- 西安会議(AMF-1 & ICECM-ICSA '95)
- 2PC-1 PbZrO_3系セラミックスの相転移点近傍での圧電性(圧電応用デバイス・振動子,ポスターセッション(概要講演))
- D-1 粒子配向ビスマス層状構造強誘電体セラミックスのSAW特性(表面弾性波とデバイスI)
- 電子セラミックスの最先端研究動向と将来展望
- 3D32 (Bi_Na_)TiO_3-PbTiO_3-BaTiO_3 系圧電セラミックス (II)
- Motion Characteristics Measurement of Rotating Object Using Surface Acoustic Wave Oscillator
- 1J-1 Bi_4Ti_3O_-SrBi_4Ti_4O_系非鉛圧電セラミックスの連続駆勤時におけるハイパワー圧電特性(超音波物性,フォノン物理,光超音波エレクトロニクス)
- (Bi_Na_)TiO_3-(Bi_K_)TiO_3-BaTiO_3-Based Lead-Free Piezoelectric Ceramics
- Large Piezoelectric Constant and High Curie Temperature of Lead-Free Piezoelectric Ceramic Ternary System Based on Bismuth Sodium Titanate-Bismuth Potassium Titanate-Barium Titanate near the Morphotropic Phase Boundary
- Morphotropic Phase Boundary and Electrical Properties of Bisumuth Sodium Titanate-Potassium Niobate Solid-Solution Ceramics
- (Li_Bi_)で変性したPZT系セラミックスの相境界近傍での圧電温度特性 : 物性・応用
- B-4 PbTiO_3系強誘電体セラミックスの圧電的性質(超音波の発生・検出I)
- 2-15 粒子配向型圧電セラミックスの作成法と電気的性質(一般講演)
- (Bi_Na_)TiO_3-BaTiO_3 System for Lead-Free Piezoelectric Ceramics : Piezoelectrics
- 高温圧電センサ応用にむけた強誘電体セラミックスの開発
- 高温用圧電材料の探索 (第28回エレクトロセラミックスセミナー フロンティア 高温電子セラミックス--パワーエレクトロニクス、エネルギーシステムの革新)
- Preliminary Results of Magnetic Resonance Imaging-aided High-dose-rate Interstitial Brachytherapy for Recurrent Uterine Carcinoma after Curative Surgery
- Formation of morphotropic phase boundary and electrical properties of (Bi1/2Na1/2)TiO3-Ba(Al1/2Nb1/2)O3 solid solution ceramics (Special issue: Ferroelectric materials and their applications)
- Current developments and prospective of lead-free piezoelectric ceramics (Special issue: Ultrasonic electronics)
- Grain-Size Effect on Electrical Properties of (Bi_K_)TiO_3 Ceramics
- P1-2 Piezoelectric Properties of (Bi_Na_)TiO_3-based Ferroelectric Ceramics(Poster session 1)
- Ferroelectric and Piezoelectric Properties of (Bi_K_)TiO_3 Ceramics
- (Bi1/2Na1/2)TiO3-(Bil/2K1/2)TiO3-BaTiO3-Based Lead-Free Piezoelectric Ceramics (Special Issue Ultrasonic Electronics)
- Piezoelectric Properties of BaTiO_3-(Bi_K_)TiO_3 Ferroelectric Ceramics
- Preparation and Characterization of ZnO and (Zn,Mg)O films doped with Al
- Electrostrictive Properties of Pb(Mg_Nb_)O_3-Based Relaxor Ferroelectric Ceramics
- Antibiotic treatment for bacterial meningitis caused by Listeria monocytogenes in a patient with multiple myeloma
- Propagation Characteristics of Lamb Waves in PbZrO_3-Based Ceramic Substrate
- Automated Piezoelectric Measurement System and Its Application to BLSF Ceramics : P: PIEZOELECTRICS
- Composite Piezoelectric Ceramics of (LiBi)_-Modifed PZT System : F: FERROELECTRIC MATERIALS
- Acoustic Wave Characteristics of Lead-Free (Bi_Na_)_Ca_TiO_3 Piezoelectric Ceramic : F: FERROELECTRIC MATERIALS
- Superconducting Properties of Grain-Oriented YBa_2Cu_3O_ Ceramics : Electrical Properties of Condensed Matter
- Piezoelectric Properties of Solid-Solution (Bi_(PbBa)_x)(Ni_Ti_)O_3 Ceramics ( FERROELECTRIC MATERIALS AND THEIR APPLICATIONS)
- KNbO3系非鉛強誘電体セラミックスの大振幅圧電特性
- Bi_M_xTiTa0_9 (M=La or Nd) Ceramics with High Mechanical Quality Factor Q_m
- Lead-Free Piezoelectric Ceramics of (Bi1/2Na1/2)TiO3–KNbO3–1/2(Bi2O3·Sc2O3) System
- 90° Domain Reorientation and Electric-Field-Induced Strain of Tetragonal Lead Zirconate Titanate Ceramics
- 変調構造酸化亜鉛とその電気伝導性
- A New Series of Bismuth Layer-Structured Ferroelectrics
- Piezoelectric and Pyroelectric Composite Ceramics of the Multilayer Type by Tape Casting : F: FERROELECTRIC MATERIALS
- 強誘電特性の巨大異方性を有する粒子配向セラミックス (特集 巨大機能物性を生むセラミックス)
- ビスマス系非鉛強誘電体セラミックスのハイパワー圧電特性
- KNbO_3 系非鉛強誘電体セラミックスの大振幅圧電特性
- 圧電材料・デバイス : 特集号によせて
- 3Pa1-6 (Bi_Na_)TiO_3系非鉛圧電セラミックスのハイパワー特性に及ぼすMn添加・置換効果(ポスターセッション)