液体急冷した6.6%珪素鉄薄帯の表面エネルギーによる異常粒成長

概要

論文の詳細を見る
In order to understand the mechanism of abnormal grain growth in melt-quenched Fe-6.6%Si ribbons the recrystallization process during high temperature annealing has been investigated. Abnormal grain growth occurs at temperatures between 1273 and 1473K in vacuum, dry hydrogen or dry argon atmosphere. The preferred orientation of the abnormal grain growth depends on annealing temperature and atmosphere sensitively. In the vacuum of total pressure from 6×10^<-3> to 10 Pa, highly oriented {110} <uuw> and {100} <0 vw> textures form under the conditions of higher temperature-lower pressure and lower temperature-higher pressure respectively. In the hydrogen and the argon atmospheres with dew point of 228K, strong {110} <uuw> and {100} <0 vw> oriented textures are also observed respectively. Such an abnormal grain growth can be explained in terms of the surface energy differences between the crystallographic planes, and the surface energy itself is also affected by the oxidation.
社団法人日本鉄鋼協会の論文
1988-06-01