赤スケール生成におよぼす熱間圧延条件と高圧水デスケーリングの影響

概要

論文の詳細を見る
Red scale defects usually observed in high Si hot rolled strip were reproduced in a laboratory 3 stand tandem mill. The effects of hot rolling and descaling condition on the strip surface color and scale structure were examined. Irrespective of Si content in steel, the hot rolled strip surface became red when the scale thickness before rolling was above 20 μm and the rolling temperature was below 900℃. It was found that surface part of the scale (mainly FeO) was broken to powder by the hot rolling at the temperature below 900℃. The red scale of Fe_2O_3 was formed by the oxidation of powdered scale during cooling. Thick scale formed during slab soaking was completely removed by hydraulic descaling before rolling in low Si steel, whereas that was not removed in high Si steel. This remained scale caused the red scale defects after rolling and cooling. The application of obtained results to the hot strip mill production of red scaleless strip was discussed.
社団法人日本鉄鋼協会の論文
1994-11-01