箱焼鈍法による焼付硬化性 Al キルド冷延鋼板(冷延鋼板)(<特集>高強度薄鋼板)

概要

論文の詳細を見る
The bake-hardenable cold-rolled steel sheets for the outer panels of auto-bodies exhibiting a sufficient formability and an excellent resistance to denting have been developed in box-annealing process. Examinations in the effects of chemical composition and box-annealing condition on the bake-hardenability and on Snoek peak height of Al-killed steels revealed that lowering total carbon content to less than 0.02% for tight coil annealing and raising annealing temperature to α/γ intercritical range for open coil annealing, besides, adding silicon or phosphorus and reducing manganese content in steel can increase the bake-hardenability to 40 MPa, retaining 10ppm carbon in solution. The mill produced bake-hardenable Al-killed steel sheets showed practically non-aging quality and high r-value. Discussions were made on the compatibility of retarded aging property and bake-hardenability of the steels by using Hundy's equation. A retarded aging and bake-hardenable rimmed steel was also produced by controlling nitrogen to 8 ppm in the open coil annealing furnace.
社団法人日本鉄鋼協会の論文
1982-07-01