Preparation of Double-Sided YBCO Films on LaAlO_3 by MOD Using Commercially Available Coating Solution(<Special Section> Superconducting High-frequency Devices)

スポンサーリンク

概要

• 論文の詳細を見る

• The 5-cm-diameter double-sided YBa_2Cu_3O_7 (YBCO) films were prepared by metal organic deposition (MOD) using a commercially available metal-naphthenate coating solution. Firstly, YBCO film was prepared by MOD on one side of a double-side-polished 5-cm-diameter LaAlO_3 substrate. Secondly, another side was similarly coated with YBCO by MOD. After the latter processing, degradation of average J_c value in the first side was not observed; but the fluctuation of critical current density J_c slightly increased. The double-sided YBCO films showed average J_c values of 0.8-1.0MA/cm^2 at 77K and microwave surface resistances R_s(12GHz) of 0.86-1.07mΩ at 70K.

• 社団法人電子情報通信学会の論文
• 2006-02-01

著者

• MANABE Takaaki

  National Institute of Advanced Industrial Science and Technology

• KUMAGAI Toshiya

  National Institute of Advanced Industrial Science and Technology

• YAMAGUCHI Iwao

  National Institute of Advanced Industrial Science and Technology (AIST)

• AHN Jun

  National Institute of Advance Industrial Science and Technology (AIST)

• SOHMA Mitsugu

  National Institute of Advance Industrial Science and Technology (AIST)

• KONDO Wakichi

  National Institute of Advance Industrial Science and Technology (AIST)

• TSUKADA Ken-ichi

  National Institute of Advance Industrial Science and Technology (AIST)

• KAMIYA Kunio

  National Institute of Advance Industrial Science and Technology (AIST)

• MIZUTA Susumu

  National Institute of Advance Industrial Science and Technology (AIST)

• TSUKADA Kenichi

  National Institute of Advanced Industrial Science and Technology (AIST)

• Kumagai T

  Advanced Manufacturing Research Institute National Institute Of Advanced Industrial Science And Tech

• Mizuta S

  National Institute Of Advanced Industrial Science And Technology (aist)

• Kondo Wakichi

  National Institute Of Advanced Industrial Science And Technology (aist)

• Kumagai Toshiya

  National Inst. Advanced Industrial Sci. And Technol. (aist) Ibaraki Jpn

• Sohma Mitsugu

  National Institute Of Advanced Industrial Science And Technology (aist)

• Sohma Mitsugu

  National Chemical Laboratory For Industry

• Mizuta Satoru

  National Institute Of Advanced Industrial Science And Technology (aist)

• Kamiya Kunio

  National Institute Of Advanced Industrial Science And Technology (aist)

• Manabe Takaaki

  National Institute Of Advanced Industrial Science And Technology (aist)

• Yamaguchi I

  National Institute Of Advanced Industrial Science And Technology (aist)

• Ahn Jun

  National Institute Of Advance Industrial Science And Technology (aist):chonnam National University

• Mizuta Susumu

  National Institute of Advanced Industrial Science and Technology (AIST)

• KUMAGAI Toshiya

  Advanced Manufacturing Research Institute, National Institute of Advanced Industrial Science and Technology

• Manabe Takaaki

  National Institute of Advance Industrial Science and Technology (AIST)

• Kumagai Toshiya

  National Chemical Laboratory for Industry

• Mizuta Susumu

  National Chemical Laboratory for Industry

• Kondo Wakichi

  National Chemical Laboratory for Industry

関連論文

• Synthesis and Surface Acoustic Wave Property of Aluminum Nitride Thin Films Fabricated on Silicon and Diamond Substrates Using the Sputtering Method : Surfaces, Interfaces, and Films
• Preparation of polycrystalline VO2 films on glass and TiO2/glass substrates by means of excimer laser assisted metal organic deposition
• Epitaxial growth of La_Ba_MnO_3 thin films on SrTiO_3 and LaAlO_3 substrates by metal-organic deposition process
• Preparation of Double-Sided YBCO Films on LaAlO_3 by MOD Using Commercially Available Coating Solution( Superconducting High-frequency Devices)
• Fabrication of Double-Sided YBa_2Cu_3O_7 Films on CeO_2-Buffered Sapphire Substrates by MOD Process( Superconducting High-frequency Devices)
• Electrical Properties of La_Ca_MnO_3 Thin Films Obtained by Metal-Organic Deposition (MOD) using Excimer Laser and Thermal Annealing
• Preparation of High-J_c YBa_2 Cu_3O_ Films on CeO_2-Buffered Yttria-Stabilized Zirconia Substrates by Fluorine-Free Metalorganic Deposition
• Large Temperature Coefficient of Resistance in La_Ca_MnO_3 Thin Films Obtained by Metal Organic Deposition Process
• Low Temperature Growth of Epitaxial La_Sr_MnO_3 Thin Films by an Excimer-Laser-Assisted Coating Pyrolysis Process
• Preparation of Epitaxial YBa_2Cu_3O_/CeO_2 Multilayer Films on Yttria-stabilized Zirconia (100) by All-Coating-Pyrolysis Process : Superconductors
• Preparation of PbTiO_3 Thin Films Using a Coating Photolysis Process with ArF Excimer Laser
• X-Ray Diffraction Studies of Epitaxial La_Sr_CoO_3 Thin Films Prepared by the Dipping-Pyrolysis Process
• Direct Conversion of Metal Acetylacetonates and Metal Organic Acid Salts into Metal Oxides Thin Films Using Coating Photolysis Process with An ArF Excimer Laser
• Direct Conversion of Titanium Alkoxide into Crystallized TiO_2 (rutile) Using Coating Photolysis Process with ArF Excimer Laser
• Epitaxial Growth of Bi_4Ti_3O_ Thin Films on LaAlO_3 (012) and MgO (100) by Dipping-Pyrolysis Process
• Preparation of Epitaxial Pb(Zr, Ti)O_3 Thin Films on Nb-Doped SrTiO_3(100) Substrates by Dipping-Pyrolysis Process
• Effective-Time of Pulsed Photothermal Heating for Polycrystalline Nucleation of Perovskite Oxide Films from an Amorphous Matrix
• Low-temperature fabrication of red phosphor Ca0.997Pr0.002TiO3 thin film using excimer laser assisted metal organic deposition
• Critical Current Densities at 77 K in Ba_2YCu_3O_-Ag Films Prepared by Dipping-Pyrolysis Process
• Preparation and Superconducting Properties of Bi-Pb-Sr-Ca-Cu-O Films (T_c=106 K) by the Dipping-Pyrolysis Process
• Preparation of High-J_c Ba_2YCu_3O_ Films on SrTiO_3 (100) Substrates by the Dipping-Pyrolysis Process at 750℃
• Preparation of Superconducting Ba_2YCu_3O_/Ag Composite Films by the Dipping-Pyrolysis Process Using Metal Naphthenates at 750℃
• Effects of Annealing Conditions and Substrate Materials on the Superconducting Properties of Ba_2YCu_3O_ Films Prepared by the Dipping-Pyrolysis Process at 750℃
• Preparation of Superconducting Ba_2YCu_3O_ Films by the Dipping-Pyrolysis Process at 700° and 750℃
• Effects of Heat Treatment Conditions on the Critical Current Densities of Ba_2YCu_3O_ Films Prepared by the Dipping-Pyrolysis Process
• Mechanism of Degradation in Hydrous Electrorheological(ER)Systems
• The effect of surface characteristics of silica particles on electrorheology
• Chemically assisted dry comminution of an inorganic powder
• Effect of Ion Implantations and Post-treatments on Optical Transmission of Fluorozirconate Glass
• Polarization Properties in Phase Conjugation with Bacteriorhodopsin
• Optical Characterization of Ion-Implanted Glass Surface Layers with Surface Plasmon Resonance Method
• Fusion of Paramecia by Means of Altered Electrofusion
• Diffusion of Electrolyte in Shrunken Polyacrylamide Gel
• Emission Characteristics of Internally Self-Pumped Phase-Conjugate Wave in Photorefractive KNbO_3:Fe and BaTiO_3 Crystals
• Temperature Dependence of Magnetization and Electrical Resistivity of Weak Itinerant Ferromagnetic Pd in NiO/Pd Multilayers
• Appearance of Ferromagnetism Induced by Proximity Effect and Exchange Enhancement in Multilayer Consisting of Antiferromagnetic Nio and Paramagnetic Pd
• Adjustment of thermal hysteresis in epitaxial VO2 films by doping metal ions
• Three Types of Ternary Selenides with Layered Composite Crystal Structures Formed in the Pb-Nb-Se System
• Preparation of Superconducting Niobium Nitride Films by Molecular Beam Epitaxy Method
• Ti-Doped VO2 Films Grown on Glass Substrates by Excimer-Laser-Assisted Metal Organic Deposition Process
• Preparation of YBa2Cu3O7-δ Micropatterns Using Metal–Organic Deposition with Electron Beam
• Epitaxial Growth of La0.7Ba0.3MnO3 Thin Films on SrTiO3 and LaAlO3 Substrates by Metal-Organic Deposition
• Electrical Properties of La0.7Ca0.3MnO3 Thin Films Obtained by Metal-Organic Deposition (MOD) using Excimer Laser and Thermal Annealing
• Preparation and Characterization of Epitaxial VO2 Films on Sapphire Using Postepitaxial Topotaxy Route via Epitaxial V2O3 Films
• Low-Temperature Fabrication of Red Phosphor Ca0.997Pr0.002TiO3 Thin Film Using Excimer Laser Assisted Metal Organic Deposition
• Preparation of High-$J_{\text{c}}$ YBa2Cu3O7-y Films on CeO2-Buffered Yttria-Stabilized Zirconia Substrates by Fluorine-Free Metalorganic Deposition
• Kinetics of the catalytic decomposition of hydrogen iodide in the magnesium-iodine thermochemical cycle.

もっと見る 閉じる

スポンサーリンク