V/III Flux Ratio Dependence of InAs Epilayers Grown on GaAs Subsutrates by Molecular Beam Epitaxy
スポンサーリンク
概要
- 論文の詳細を見る
InAs epilayers 2 μm thick were grown on (100) GaAs substrates. Under the As stabilized condition, the epilayer growth progresses in the mode of 2-dimensional (2D)-3D-2D growth. The lattice constant changes sharply from that of GaAs to the bulk value of InAs in the early stage of growth. A high density of small islands are formed in the initial stage and strain due to lattice mismatching is relaxed by the occurrence of island merging. As a result, the 2-μm-thick epilayers show smooth surface morphology and high electrical quality. On the other hand, when the epilayer growth is carried out under the In-stabilized condition, the lattice constant shows two-step saturation. The lattice constant saturates once in the initial stage, and after some time begins to increase toward the bulk value of InAs. In this case, the island density is low and each island grows laterally. Then, rather large strain is incorporated in the epilayers even after island merging and, as a result, dislocations are widely distributed in the latter half of epilayer growth. As a result, the 2-μm-thick epilayers show rather rough surface morphology, and the electrical properties also deteriorate.
- 社団法人応用物理学会の論文
- 1994-06-15
著者
-
Okamoto Kotaro
Department Of Electronics Engineering Shizuoka University
-
Okamoto Kotaro
Department Of Communication Engineering University Of Electro-communications
-
HANANOKI Ryoji
Department of Electronic Engineering, University of Electro-Communications
-
Hananoki Ryoji
Department Of Electronic Engineering University Of Electro-communications
関連論文
- Selective Epitaxial Growth of GaAs by Metalorganic Chemical Vapor Deposition
- Doping Properties of GaAs Selective Epilayers Grown by Atmospheric-Pressure Metalorganic Chemical Vapor Deposition
- V/III Flux Ratio Dependence of InAs Epilayers Grown on GaAs Subsutrates by Molecular Beam Epitaxy
- InGaAs Epilayers of High In Composition Grown on GaAs Substrates by Molecular Beam Epitaxy
- Lateral Supply Mechanisms in Selective Metalorganic Chemical Vapor Deposition
- Anisotropic Ridge Growth by Step-Flow-Mode Metalorganic Chemical Vapor Deposition Using Diethylgalliumchloride
- MES-FETs Fabricated on Doped a-Si Films
- Metalorganic Chemical Vapor Deposition of GaAs on (111)B Substrates by Using Diethylgalliumchloride