Study on Weld Crackings in Ni-Base Superalloy, Inconel 713C
スポンサーリンク
概要
- 論文の詳細を見る
Weld crackings occurring in Inconel 713C are hot crackings. The main cause of hot crackings is low melting point white constituents crystallized at grain boundaries. The formation of harmful white constituents can be prevented with increasing C content or decreasing γ′ phase forming elements such as Al, Nb and Ti. Increasing the C content (adding 0.2∿0.3% C) is extremely effective to improve the hot cracking sensitivity of Inconel 713C under low restraint conditions, attaching importance to mechanical properties at high temperature.
- 社団法人溶接学会の論文
著者
-
Ikawa Hiroshi
Faculty Of Engineering Osaka University
-
Ikawa Hiroshi
Faculty Of Engineering Osaka University Yamadakami
-
NAKAO Yoshikuni
Faculty of Engineering, Osaka University
-
SHIN Shigeo
Faculty of Engineering, Osaka University
-
Shin Shigeo
Faculty Of Engineering Osaka University Yamadakami
-
Shin Shigeo
Faculty Of Engineering Osaka University
-
Nakao Yoshikuni
Faculty Of Engineering Osaka Univ.
関連論文
- Fractogrphy on Microcracks in Ni-base Multipass Weld Metals : Study on Microcracks in Multipass Weld Metals of Ni-base Alloys (Part 1)
- Effects of Cr and S on Ductility-dip Cracking Susceptibilities in the Reheated Weld Metals of Ni-Cr-Fe Ternary Alloys : Study on Microcracks in Multipass Weld Metals of Ni-base Alloys (Part 2)
- Effects of Rapid Solidification by Laser Surface Melting on Solidification Modes and Microstructures of Stainless Steels
- Study on the Knife Line Attack Phenomenon in Stabilized Austenitic Stainless Steels : Mechanism and Improvement by Addition of REM
- Application of Grain Growth Equation to the Selection of Welding Conditions
- Austenite Grain Growth of Steels during Thermal Cycles
- Grain Growth of Commercial-Purity Nickel in Weld-Heat Affected Zone
- Quantitative Analysis on Grain Growth of Commercial-Purity Nickel during Various Weld Thermal Cycles
- Relation between Welding Conditions and Grain Size in Weld-Heat Affected Zone
- Calculation of Grain Size in Weld-Heat Affected Zone Using Heat Conduction Equation
- Austenite Grain Growth of Steel in Weld-Heat Affected Zone
- Study on Hot Cracks in Cast Ni-Base Superalloy, B-1900
- Study on Weld Crackings in Ni-Base Superalloy, Inconel 713C
- Bonding Mechanism in Transient Liquid Insert Metal Diffusion Bonding Using Alloying Powder : Study on Transient Liquid Insert Metal Diffusion Bonding of Ni-base Superalloys (Part 7)
- Newly Development in Transient Liquid Insert Metal Diffusion Bonding Using Alloying Powder : Study on Transient Liquid Insert Metal Diffusion Bonding of Ni-base Superalloys (Part 6)
- Theoretical Considerations on the Metallurgical Process in T.L.P. Bonding of Nickel-Base Superalloys
- Study on Weldability of Dispersion Hardening Alloy
- Transient Liquid Phase (T.L.P.) Diffusion Bonding of Nickel-Base Heat Resisting Alloys
- Effect of Rapid Solidification on Pitting Corrosion Resistance in Weld Metals of Mo Containing Stainless Steels : Study on Surface Modification of Stainless Steels by Laser Surface Melting (Report 7)
- Effect of Rapid Solidification on Corrosion Resistance of Stainless Steels : Study on Surface Modification of Stainless Steels by Laser Surface Melting (Report 6)
- Effect of Rapid Solidification on the Delta-ferrite Content in Microstructure and Its Implications on the Schaeffler diagram : Study on Surface Modification of Stainless Steels by Laser Surface Melting (Report 5)
- Effect of Rapid Solidification on the Microstructures and Delta-ferrite Morphologies : Study on Surface Modification of Stainless Steels by Laser Surface Melting (Report 4)
- Study on Reheat Cracking of Ni-base Superally, Waspaloy
- Desensitization of Stainless Steels by Laser Surface Heat-Treatment