アーク抵抗の統計的研究
スポンサーリンク
概要
- 論文の詳細を見る
Generally the fluctuation of are resistance of electrical insulating materials is remarkably large even if the tests are carried out under the same condition with the same testing aparatus. In this paper, the cause of the fluctuation of arc resistance was discussed form the results of arc resistance test on a large number of specimens. The experimental method was nearly same as the ASTM D492-71 and various plastics was used as the test materials. For each materials. For each material, 80-100 tests were carried out The main results obtained are as follows: (1) The Frequency curve of arc resistance generally has plus skewness and can be represented approximately by a logarithmic normal distribution. Furthermore, this distribution curve agrees well with the result of calculation obtained by considering a stochastic process. Thus, it is considered that the phenomenon of arc deterioration is a statistical one. (2) The loading with fillers, the temperature rise of circumference and the increase of test voltage equally decrease the fluctuation of arc resistance. (3) No significant difference is observed on the fluctuation of arc resistance between the test with rod electrode and that with rectangular plate electrode in ASTM method. (4) it is convenient to elucidate the fluctuation of arc resistance when the probability of arc deterioration p is introduced. This value of p can be obtained from the slope of log r-t curves, r being the non-deterioration probability. Moreover, p is small at the beginning but reaches nearly constant after a while. (5) The non-deterioration probability can estimated when the log r-t curve is available. Even if the recurrent speed of discharge is different in each test as in the ASTM method, the non-deterioration probability r can be derived by using a number of the log r-t curves corresponding to each of the test steps.
- 社団法人日本材料学会の論文
- 1979-04-15
著者
関連論文
- ポリエステル樹脂の耐アーク性について
- 電気絶縁材料の耐アーク性に及ぼす印可電圧波形の影響
- プラスチックの耐アーク性試験について
- 大きい電極ギャップ長における合成樹脂のアーク劣化の研究
- 電気絶縁材料の耐ア-ク性の評価に関する研究
- 円柱状合成樹脂試料の耐ア-ク性について
- Si,GaAsおよびInP太陽電池の出力特性の温度依存性解析
- 粉体の静電混合に関する研究
- 永久磁石の反発力を利用した無捲線モ-タの研究
- トロリ-線を除去した電鉄き電回路の構成に関する研究