電気絶縁材料の耐アーク性に及ぼす印可電圧波形の影響
スポンサーリンク
概要
- 論文の詳細を見る
There are many cases that the alternating voltage applied on the practical electrical machines contains not only constant amplitude sinusoidal waves but also distorted waves or high frequency-superimposed waves. Therefore, the real appraisal of arc resistance of insulating materials for such applications is difficult to make on the basis of arc resistance determined by the conventional test under sinusoidal wave voltage. In this paper, the arc resistance under distorted wave voltage and high frequency-superimposed wave voltage were investigated. The test method was similar to the high voltage low current arc resistance test like the ASTM method. However, the test method using the triac was tried in order to search for a reliable arc resistance test which incorporates the merits of the electrical static type interrupter of circuit and compensates the weakness of the mechanical intermittent interrupter. The applied voltage, arc current and arc intermittent time of the fundamental waves for the high voltage low current arc test were the same as used in the ASTM method. The electrode type was the rod type and the electrode gap length was 6.4 mm. To generate distorted wave voltage and high frequency-superimposed one, the voltage from the oscilator was amplified separately as in Fig. 2 and was superimposed to the fundamental sinusoidal wave at the secondary side of the transformer. The results of the tests show that the arc resistance decreased with increasing frequency of the superimposed wave and also with increasing crest value of the waves at a constant frequency, when the high frequency voltage was superimposed and its crest value was about 4-20% of the fundamental sinusoidal wave voltage, Furthermore, the above arc resistance was lower than the one at the smooth sinusoidal wave voltage with the same maximum and minimum voltages.
- 1978-10-15
著者
関連論文
- ポリエステル樹脂の耐アーク性について
- 電気絶縁材料の耐アーク性に及ぼす印可電圧波形の影響
- プラスチックの耐アーク性試験について
- 大きい電極ギャップ長における合成樹脂のアーク劣化の研究
- 電気絶縁材料の耐ア-ク性の評価に関する研究
- 円柱状合成樹脂試料の耐ア-ク性について
- Si,GaAsおよびInP太陽電池の出力特性の温度依存性解析
- 粉体の静電混合に関する研究
- 永久磁石の反発力を利用した無捲線モ-タの研究
- トロリ-線を除去した電鉄き電回路の構成に関する研究