大きい電極ギャップ長における合成樹脂のアーク劣化の研究
スポンサーリンク
概要
- 論文の詳細を見る
Many studies on arc deterioration of electrical insulating materials by high voltage-low current arc have hitherto been done by using small size samples with electrodes having short gap length. In this paper, the arc resistance tests different from the previous ones were carried out by applying higher voltage and longer electrode gap length than before. Arc resistance was measured by a new arc resistance test method and the process of arc deterioration was investigated. As the experimental method, ASTM D495 standard test method was modified a little. Electrodes were the stainless steel plate type of 5〜100 mm in length and the applied voltage was max. 100 kV. Furthermore, arc resistance in the case of electrodes detouched from the sample surface was also investigated. The experimental results are summarized as follows: (1) The arc resistance of insulating materials measured with contact electrodes having long gap length showed two different tendencies depending upon the species of insulating materials, one showing a slow increase with increasing gap length from about 40 mm to 100 mm, and the other a tendency of saturation at the gap length of 50 mm or more. Thus, the effect of electrode gap length on arc resistance was observed clearly (2) The arc resistance of insulating materials measured with detouched electrodes having long gap length also showed two different tendencies depending upon the species of insulating materials, one showing a slow increase with increasing gap length from about 30〜40 mm to 100 mm and the other nearly constant. Thus, the separation of electrodes from the sample surface affected arc resistance remarkably and the effect of electrode gap length on arc resistance was observed in this case also. (3) The effect of spatial configuration of sample on the arc resistance of insulating materials exists not only in comparatively small electrode gap length but also in long one.
- 社団法人日本材料学会の論文
- 1986-04-15
著者
関連論文
- ポリエステル樹脂の耐アーク性について
- 多層カーボンナノチューブを用いた水素ガスセンサ(有機薄膜・複合膜とデバイス応用,一般)
- 多層カーボンナノチューブを用いた水素ガスセンサ
- 電気絶縁材料の耐アーク性に及ぼす印可電圧波形の影響
- 有機色素ドープ高分子フィルムの負性抵抗特性
- プラスチックの耐アーク性試験について
- 大きい電極ギャップ長における合成樹脂のアーク劣化の研究
- 電気絶縁材料の耐ア-ク性の評価に関する研究
- 円柱状合成樹脂試料の耐ア-ク性について
- 系統補償直列コンデンサの設置地点について
- Si,GaAsおよびInP太陽電池の出力特性の温度依存性解析
- 粉体の静電混合に関する研究
- 永久磁石の反発力を利用した無捲線モ-タの研究
- トロリ-線を除去した電鉄き電回路の構成に関する研究
- 合成樹脂の耐アーク性時間 : 印加電圧曲線の一誘導法
- 合成樹脂の耐トラッキング性試験の一つの試み
- 合成樹脂の耐アーク性試験
- 磁路による電力輸送の基礎的研究
- 模型飛行機による自然環境のパタ-ン計測
- 太陽熱を揚水に利用した水力発電方式の研究
- 液体絶縁体中における合成樹脂の耐アーク性
- 低温における合成樹脂の耐アーク性
- ガス絶縁体中における合成樹脂の耐アーク性
- 電気絶縁材料表面のトリーイング劣化
- アーク抵抗の統計的研究
- 複合硬化剤を用いたエポキシ樹脂の耐アーク性について
- 電極を試料面より隔離した場合における電気絶縁材料の耐アーク性に及ぼす試料の寸法効果
- 実用機器絶縁構成における電気絶縁材料の耐アーク性の問題点ならびにアーク劣化過程の研究
- 電気絶縁材料の耐アーク性に及ぼす試料の空間配置の効果
- 電極を試料面より隔離した高電圧小電流耐アーク性試験
- 有機質絶縁材料の耐アーク性と化学構造との関係
- エポキシ樹脂の電気伝導と絶縁破壊
- エポキシ樹脂の電気的特性におよぼすγ線照射の影響
- エポキシ樹脂の電気的特性におよぼす紫外線の影響
- エポキシ樹脂洋鉱物質充てん剤について
- 電気絶縁材料の耐アーク性に及ぼす試面の幾何学的形状の影響
- 化学〓による耐アーク性の測定
- 高電圧小電流アークによる絶縁材料の劣化について
- 電極と絶縁材料の組合せ配置時の耐アーク性