ひずみ範囲分割法によるボイラ管寄せリガメント部のクリープ疲労寿命評価

概要

論文の詳細を見る
Strain range partitioning method was applied to creep-fatigue life prediction for ligaments of high temperature boiler headers. Typical operating transient data was used to conduct thermal transient analysis and elastic-plasticcreep stress analysis with three dimensional FEM models simulating ligament parts of headers. Creep-fatigue life was predicted by strain range partitioning method based on the analytical results and creep-fatigue properties of a header material. The results obtained were as follows. (1)Cracking was expected in ligament parts with inelastic strain produced by thermal transient during start-up and shut-down operation. (2)The points where ligament crack was predicted to initiate coincided with ones reported in actual plants failure cases. (3)The effects of operational condition and size of header on ligament crack initiation life were evaluated by this analysis. It was found that the ligament crack initiation life tends to be shorter in the case of the faster ramp rate and the larger header diameter.
社団法人日本材料学会の論文
1999-06-15