電場が温水処理に伴う SiO_2-TiO_2 系ゲルコーティング膜のチタニア微結晶生成に及ぼす影響

概要

論文の詳細を見る
Sol-gel derived SiO_2-TiO_2 coatings on indium tin oxide (ITO)-coated glass substrates were treated with hot water at 90℃ under electric field aiming at the control of morphology and crystalline phase of the titania precipitates. The shape of the precipitates on 75SiO_2・25TiO_2 (mol%) coating at the negative electrode changed from granular to ramiform by applying an electric field to the substrates during the treatment, whereas such changes in the shape of titania nanocrystals with the electric field were not observed at the positive electrode. The granular and ramiform precipitates were identified as anatase (TiO_2) and hydrated titania (n (TiO_2)・mH_2O), respectively. The ramiform shape of the titania precipitates became significant with increasing the applied voltage, while the coatings gradually dark-colored due to the reduction of Ti^<4+> to Ti^<3+>.
社団法人日本セラミックス協会の論文
2005-04-01