概要
- 論文の詳細を見る
TiO_2 deposition on alumina powders by the hydrolysis of titanium isopropoxide ( TIP) was investigated as a model experiment of the uniform addition of a sintering aid. The rate of hydrolysis increased with increasing TIP/Al_2O_3 and H_2O/TIP molar ratios, and titania deposition occurred effectively at the H_2O/TIP ratio larger than 10. Examination of the coated powders by SEM, TEM, BET surface area measurement and electrophoresis showed that fine titania deposits adhered loosely to the alumina particles before calcination, but that after calcination at 500℃ the deposits spread over the surface of the alumna particles, resulting in the tight coating. The hydrolysis reaction was accelerated by the addition of diethylamine (DEA) ; however the titania powders had a tendency to deposit separately from the alumina particles.
- 社団法人日本セラミックス協会の論文
- 1988-03-01
著者
関連論文
- 金属ペースト用有機金化合物の合成
- 水系ゾルから作製した酸化スズ薄膜のセンサー特性
- 金属アルコキシドーDEA法によるPZT薄膜の合成と性質 : 合成・キャラクタリーゼーション
- エタノールアミンとヒドロキシケトンを修飾剤としゾルーゲル法によって作製した酸化亜鉛薄膜の微構造
- 白金で修飾したAl_2O_3/SnO_2多層膜のガスセンサー特性
- 酸化インジウム中への酸化スズの固溶限界
- 溶液法によるSnO2薄膜のパターニング
- 水蒸気及び還元性ガス雰囲気中における酸化スズ薄膜の抵抗率の経時変化
- 酸化スズ薄膜ガスセンサーのガス感度の膜厚依存性
- (26)大学院における工学教育としてのインターンシップの取り組み(第7セッション 個性化・活性化(II))
- (1) 岐阜大学工学部の学科改編・新設とカリキュラム改革 : 主として新入生に対する教育(フレッシュマンセミナー)について(第1セッション 教育システム(1))
- 金属粉末上への酸化物膜コーティング :銀粒子表面に析出させたゲル及び酸化物の形状
- 酸化スズ薄膜ガスセンサーにおけるIV族元素酸化物の添加効果
- 熱分解法による抵抗薄膜とその原材料の熱分解特性
- 熱分解法によるRuO_2-TiO_2薄膜の形成
- NbOホイスカーの選択的成長
- リン化ニオブ単結晶の気相成長
- アルミナ粉末のチタニアコーティング
- スピネル薄膜のディップ・コーティング
- ジルコニア及び混合ジルコニア薄膜のディップ・コーティング
- OMCVD法によるTiO_2-SnO_2混合薄膜の析出とその物性