焼付硬化性におよぼす結晶粒度と固溶体型強化元素の影響(機械的性質)(<特集>高強度薄鋼板)

概要

論文の詳細を見る
Effect of metallurgical factors on the bake hardenability (BH) of low carbon Al-killed steel is studied. The yield stress change due to baking (⊿YS) is determined by grain size and dissolved (C+N) content. On the other hand, the ultimate tensile stress change due to baking (⊿TS) depends mostly on the dissolved (C+N) content. The locking mechanism of dislocation is discussed in relation to grain size dependence of these properties. The influence of alloying elements (Mn, Si, and P) on BH through their metallurgical factors is also studied. Mn decreases ⊿YS through the reduction of dissolved C content. Si gives rise to the increase of dissolved C content and grain refining up to 0.5% Si content. Over 0.5% Si content, the grain becomes coarser in turn. Consequently, ⊿YS increases up to 0.5% Si content and levels off after that. Though the addition of 0.06% P does not affect the dissolved (C+N) content, it gives rise to a little increase of ⊿YS through grain refining. Larger grain size dependence of ⊿YS is observed at∿5 ppm of dissolved (C+N) content for 0.06% P containing steel.
社団法人日本鉄鋼協会の論文
1982-07-01