OS0703 マルテンサイト系ステンレス鋼の応力腐食割れおよび腐食疲労き裂進展特性の評価(構造用材料の疲労挙動と寿命評価,オーガナイズドセッション)

概要

論文の詳細を見る
This work aimed to characterize crack growth of stress corrosion cracking (SCC) and corrosion fatigue (CF) for two types of martensitic stainless steel, SUS41O and SUS41OS, in air and hydrogen environment. Crack growth characteristics were evaluated by fracture mechanics tests which were done under controlled stress intensity factor, K. Fracture mechanisms and dynamics were assessed by observing the fracture surface and adopting acoustic emission (AE) method. As the result of the tests, crack growth characteristics were evaluated and revealed the acceleration under the hydrogen environment. Based on the AE analysis, it was considered that the hydrogen embrittlement cracking occurred more frequently in CF test around the maximum applied load. The observation of the fracture surface suggested that the significant embrittlement of the materials by the effect of hydrogen, and the hydrogen embrifflement cracking occurred near the surface of specimen where hydrogen diffused more quicidy.
一般社団法人日本機械学会の論文
2009-07-24