1573Kにおける固体Fe-Cr合金中の硫黄の活量ならびに同合金と硫化物との平衡
スポンサーリンク
概要
- 論文の詳細を見る
Equilibrium between solid iron-chromium alloys and H_2-H_2S gas mixture was measured using a gas circulating method, to determine the activity of sulfur in the alloys at 1573K. An isothermal section of the Fe-Cr-S system at 1573K was experimentally determined over the metal/sulfide equilibrium region using a conventional silica capsule technique. The thermodynamic evaluation procedure based on a modified GIBBS-DUHEM integration was applied to the experimentally obtained tie-line distribution and phase relations, and a stability diagram was obtained. This revealed the existence of stable fields of the metal and sulfide phases as a function of the partial pressure of sulfur and the metal ratio. The solubility of sulfur in the Fe-Cr alloy was also determined.
- 社団法人日本鉄鋼協会の論文
- 1988-06-01
著者
-
藤澤 敏治
名古屋大学難処理人工物研究センター
-
鈴木 貴雄
名古屋大学大学院:(現)東邦ガス(株)
-
山内 睦文
名古屋大学大学院 工学研究科材料機能工学
-
藤澤 敏治
Ecotopia Science Institute Nagoya University
-
坂尾 弘
名古屋大学工学部
-
藤澤 敏治
名古屋大学大学院工学研究科 マテリアル理工学専攻
-
山内 睦文
名古屋大学大学院工学研究科マテリアル理工学専攻材料工学分野
-
浅野 正之
名古屋大学大学院
-
坂尾 弘
名古屋大学
-
浅野 正之
名古屋大学大学院:(現)愛知製鋼(株)
-
藤澤 敏治
名古屋大学 大学院工学研究科 マテリアル理工学専攻
関連論文
- 晶析逆抽出法によるNd-遷移金属混合シュウ酸塩の合成
- Sm-Co混合シュウ酸塩の熱分解過程
- 希土類 - 遷移金属混合シュウ酸塩のCa熱還元
- 高純度ネオジムの製造
- 溶融混練法により調製したシリカ/ポリスチレン系コンポジットの親水性シリカフィラー分散性と熱膨張特性
- レアアース金属の精製とその熱力学 (特集 金属素材プロセス次世代への展望) -- (ニオブ・タンタル・希土類金属)
- Si-Al-O系の熱力学
- Si-Al-O系の熱力学
- 溶銅からの不純物除去へのNa_2CO_3フラックスの適用
- 溶融シリコン中のボロンの活量