210 Ti(Pt,Ir)の高温形状記憶特性(OS9(1) 形状記憶合金の特性と応用)

概要

論文の詳細を見る
To develop high temperature shape memory alloys, TiPt and TiIr are noted because of their possibility of phase transformation above 1273K. Then, the effects of Iridium (Ir) into TiPt on the constituent phases and the phase transformation temperature were investigated. It was found that the B19 phase appeared up to 37.5at% Ir in Ti (Pt, Ir) and the phase transformation temperature raised from 1303K in TiPt to 1473K in the Ti-12.5Pt-37.5Ir. Shape recovery and superelasticity of Ti-50 (Pt, Ir) were investigated by thermal expansion measurement in dilatometer and loading-unloading compression test. The shape recovery was found in all compounds in at least one of the testing methods. The highest shape recovery, about 4% was found in Ti-25Pt-25Ir using loading-unloading compression test. On the other hand, superelasticity was found in only ternary compounds. Larger superelasticity was observed in ternary compounds with higher Ir contents. Potential of Ti-50 (Pt, Ir) as high-temperature shape memory alloys is discussed.
一般社団法人日本機械学会の論文
2006-08-03