On the Equilibrium among Silicon in Molten Iron, Blast Furnace Slag and H_2-H_2O Mixed Gas. I : Measurement of the Equilibrium among Silicon in Molten Iron, SiO_2-CaO Binary Slag and H_2-H_2O Mixed Gas
スポンサーリンク
概要
- 論文の詳細を見る
1. Measurement of Equilibrium of the Reaction, (SiO_2)^<**>_<sat>+2H_2=Si^<**>+2H_2O The reduction of silica from molten slag to molten iron by H_2 gas is one of the important reactions in iron and steel making process which may be expressed in the equation as follows : (SiO_2)+2H_2=Si+2H_2O……(1) When the slag is saturated with SiO_2, equation (1) becomes (SiO_2)_sat.+2H_2=Si+2H_2O……(2) As the direct measurement of the equilibrium of equation (1) was difficult, the equilibrium of equation (2) was measured, using a pure silica crucibe in the temperature range from 1, 500°to 1, 600℃. From the experimental results, it was found (a) that the relation between p^2H_2/p^2H_2O and Si% at a given temperature could be expressed by a straight line and (b) that the temperature function of the equilibrium constant could be expressed as follows : Chemical formula. 2. Measurement of the Equilibrium of the Reaction, (SiO_2)_<cao sat.>+2H_2=Si+2H_2O The equilibrium of this reaction was measured in the temperature range from 1, 550° to 1, 650℃, using a pure CaO crucible^<***> and a SiO_2-CaO binary slag in which SiO_2 content was about 60% From the results of measurement, the values of the activity of SiO_2 on the liquidus line at 1, 550°, 1, 600° and 1, 650℃ were calculated as follows : a_<SiO_2> N_<SiO_2> Temperature, ℃ 0.22, 0.41, 1, 550, 0.18, 0.40, 1, 600, 0.16, 0.39, 1, 650 where pure β-cristobalite was taken as the standard of the activity of SiO_2 at each temperature. Combining these results with the data of activities of SiO_2 in SiO_2-CaO binary slags reported by Chang and Derge^<(3)>, the authors performed the thermodynamic calculation on the molten SiO_2-CaO binary slag and established the relation of equilibrium among silicon in molten iron, molten SiO_2-CaO slag and H_2-H_2O mixed gas.
- 東北大学の論文
著者
-
SANBONGI Koji
The Research Institute of Mineral Dressing and Metallurgy
-
OHTANI Masayasu
The Research Institute of Mineral Dressing and Metallurgy
-
Sanbongi K.
The Research Institute of Mineral Dressing and Metallurgy
-
Ohtani M.
The Research Institute of Mineral Dressing and Metallurgy
関連論文
- Studies on the Dephosphorization of Liquid Iron : Effect of Phosphorous on the Activity of Oxygen in Liquid Iron
- The Transfer of Carbon from a Gas Phase to Molten Iron
- Reduction Equilibria of Iron Oxides. I : Measurement of the Equilibrium of Reaction, Fe_3O_4 (in Wuestit) +CO=3FeO (in Wuestit) +CO_2
- Fundamental Study of the Structural Analysis of Monoatomic Liquids by X-ray Diffraction
- Structure of Vitreous SiO_2 and B_2O_3 by X-ray Fourier Analysis
- Effective Interionic Potentials and Properties of Molten Metals
- Research on the Activity of Components in Fundamental System of Iron Blast Furnace Slag. IV : The Activity of Lime in the System CaO-SiO_2-Al_2O_3
- Research on the Activity of Components in Fundamental System of Iron Blast Furnace Slag. II : Measurement of the Activity of Alumina in the System CaO-SiO_2-Al_2O_3
- Activities of Manganese and Carbon in Fe-C-Mn Melts
- On the Equilibrium among Silicon in Molten Iron, Blast Furnace Slag and H_2-H_2O Mixed Gas. I : Measurement of the Equilibrium among Silicon in Molten Iron, SiO_2-CaO Binary Slag and H_2-H_2O Mixed Gas
- On the Activities of Si and C in Molten Fe-Si-C Alloys
- On the Effect of Alloying Elements on the Solubility of Carbon in Molten Iron
- On the Equilibrium among Silicon in Molten Iron, Blast Furnace Slag and H_2-H_2O Mixed Gas. II : Investigation of the Equilibrium of the Reaction (SiO_2)_+2H_2=Si+2H_2O
- On Activities of Coexisting Elements in Molten Iron. II : The Activity of Silicon in Molten Fe-Si System
- On the Activities of Cr and C in Molten Fe-C-Cr Alloys
- Research on the Activity of Components in Fundamental System in Iron Blast Furnace Slag. I : Measurement of the Activity of Silica in the System of CaO-SiO_2 and CaO-SiO_2-Al_2O_3
- On the Equilibrium among Silicon in Molten Iron, Blast Furnace Slag and H_2-H_2O Mixed Gas. III : Investigation of the Equilibrium of the Reaction (SiO_2)CaO-Al_2O_3(Sat.)+2H_2=Si+2H_2O
- On the Reduction Equilibrium Diagram of Iron Oxide
- Reduction Equilibria of Iron Oxides. II : Measurement of the Equilibrium of the Reaction, FeO(1)+CO=Fe(s)+CO_2