合金粉末を用いた液相インサート金属拡散接合法の接合現象 : Ni基超耐熱合金の液相インサート金属拡散接合に関する研究(第7報)

概要

論文の詳細を見る
This paper was concerned with mechanism of isothermal solidification process on Transient Liquid Insert Metal Diffusion Bonding of Ni-base superalloys using Ni-base alloying powder. MM007 and IN100 alloys were used for base metals. IN 100 powder sheets were inserted between specimens with MBF-80 insert metal and then specimens were heated up at bonding temperatures of 1398 K. Content of liquid phase among alloying powders decreased with the lapse of bonding time. On the contrary, content of borides on dendrite boundary in alloying powders increased with the lapse of bonding time. Thermal analysis of mixed alloys with IN 100 and MBF-80 showed the possibility of crystalizing of borides in alloying powders during isothermal solidification process. It was believed concerning with the mechanism of isothermal solidification process that boron in liquid phase was consumed due to boride crystalizing in alloying powder and subsequently solid phase growth occurred in liquid phase.
社団法人溶接学会の論文
1991-11-05