Si_3N_4と金属接合界面における反応層成長に関する速度論的検討 : 耐熱性ファインセラミックスの接合に関する研究(第8報)

概要

論文の詳細を見る
Kinetics of the reaction layer growth in Si_3N_4-W brazed joints was investigated using Cu-5%Cr, Cu-1%Nb, Cu-3%V, Cu-5%Ti and Cu-10%Zr liquid insert metals. It was elucidated that the reaction layer growth could be expressed by Johnson-Mehl type equation with time exponent 'n' of 1/2. EPMA analysis of elements in the reaction layer revealed that Cr, Nb, V, Ti and Zr contents slightly decreased toward Si_3N_4,and that N content was almost constant. From the consideration of activation energy for reaction layer growth, it may be deduced that the reaction layer growth was controlled by diffusion of Cr, Nb, V, Ti and Zr in the reaction layer from the melted insert metal to Si_3N_4.