Cu富化層による熱応力緩衝効果に関する検討 : 耐熱性ファインセラミックスの接合に関する研究(第5報)

概要

論文の詳細を見る
Effects of the insert metals on the crack initiation in Si_3N_4 to SCM435 joints were investigated by paying attention to the thickness of copper enriched layer and the diameter of specimen. The 10 mm diameter joints without crack using Cu-5%Cr, Cu-1%Nb, Cu-3%V, Cu-5%Ti and Cu-10%Zr insert metals were obtained in case that the thickness of copper enriched layers were more than about 0.2 mm, 0.2 mm, 0.3 mm, 0.5 mm and 0.8 mm, respectively. As for Cu-5%Cr insert metal, the 13 mm diameter joints without crack were obtained in case of the thickness of copper enriched layer being more than about 0.4 mm. On the basis of residual stress analysis in Si_3N_4 to SCM435 joint, the critical maximum principal stress in Si_3N_4 to prevent crack in the joint were almost the same level of 350-400MPa in any cases. It was concluded that copper enriched layer had the function of relieving the thermal stress occurred in the bonding process.
社団法人溶接学会の論文
1989-08-05