An Energetic Consideration of Fatigue Mechanism of Metal under Mean Stress
スポンサーリンク
概要
- 論文の詳細を見る
It was observed that the propagation rate of fatigue crack is faster under the presence of tensile mean stress. The purpose of the present study is to give a theoretical basis of the observed characteristics of fatigue crack. At first, the energies of a crack are evaluated, the elastic energy, the surface energy, the interaction energy with external stress field and the accumulated strain energy with stress cycles. Then, the energetic conditions of crack growth are discussed. It is suggested that the process of crack propagation is devided into nearly three stages, according to the size of crack, that is, the initiation, the growth of dislocation-type crack and the propagation of semi-macroscopic crack. It follows that, the mean stress have influence on every stages, which is approximately expressed in the form pV, where p and V are the hydrostatic component of stress and the volume of crack, respectively. Various other characteristics of fatigue crack are also discussed based on the energetic consideration.
- 一般社団法人日本機械学会の論文
著者
-
Taira Shuji
Faculty Of Engineering Kyoto University
-
ABE Takeji
Assistant Professor, Faculty of Engineering, Kyoto University
-
Abe Takeji
Assistant Professor Faculty Of Engineering Kyoto University
関連論文
- Thermal Fatigue and Cyclic Mechanical Strain Fatigue at Elevated Temperature of 18-8 Cb Stainless Steel and 2.25 Cr-1 Mo Steel
- X-Ray Investigation on the Residual Stress of Metallic Materials : On the Residual Stress in Carbon Steel Caused by Thermal Stress
- Study on Fatigue Fracture in Quench-Tempered Carbon Steel : 3rd Report, On Propagation Process of Fatigue Crack
- Study on Fatigue Fracture in Quench-Tempered Carbon Steel : 2nd Report, Observation of Fatigue Crack Initiation Process by X-ray Microbeam Technique
- Study on Fatigue Fracture in Quench-Tempered Carbon Steel : 1st Report, Optical-Microscopic Observation of Fatigue Crack Initiation Process
- Creep Rupture of Internally Pressurized Cylinders at Elevated Temperatures
- X-Ray Investigation on Fatigue of Polycrystalline Metals : On the Relation between Crystal Orientation and Deformation in fcc Crystal
- Crystallographic Study of Yield Condition of Polycrystalline Metals : 1st Report, bcc Metal
- An Energetic Consideration of Fatigue Mechanism of Metal under Mean Stress
- X-ray Investigation on the Fatigue Damage of Metals
- X-Ray Investigation on Fatigue Damage of Metals under Mean Stress : 2nd Report, Torsional Fatigue
- X-Ray Investigation on Fatigue Damage of Metals under Mean Stress : (1st Report, Plane Bending Fatigue)
- X-Ray Investigation on the Prediction of Fatigue Life : On the Changes in Half-Value Breadth of Carbon Steel under Varying Stress Amplitudes
- Thermal Fatigue under Pulsating Thermal Stress Cycling
- Effect of Stress Reduction of Secondary Creep of Mild Steel
- Residual Stresses Produced by Plastic Tension in Notched Plate Specimens and Fatigue Strength
- Influence of Rest in Stress Alternation on the Fatigue Properties of a Low Carbon Steel at Elevated Temperatures
- On the Residual Stresses Due to Alternating Stressing of Annealed Steels
- Fatigue and Dynamic Creep Properties of 13 Cr Steel at Elevated Temperature under Combined Stresses of Static Tension and Alternating Bending
- Dynamic Creep and Fatigue of 13 Chromium Steel at Elevated Temperature
- X-Ray Investigation on Fatigue Fracture of Notched Steel Specimen : Observation of Fatigue Phenomena of Annealed Low-Carbon Steel by X-Ray Microbeam Technique
- X-ray Investigation of Stress Measurement : On the Method of Measurement, the Effect of Radiation Area and Resolving Power
- Crystallographic Study of Yield Condition of Polycrystalline Metals : (3rd Report, Relation between Slip in Crystals and Yield Condition)
- Creep of Mild Steel under Periodic Stresses of Rectangular Wave : (III) Prediction of the Creep Deformation under Periodic Stresses
- Creep of Mild Steel under Periodic Stresses of Rectangular Wave : (II) Creep Deformation under Unsymmetrical Periodic Stress Waves
- Creep of Mild Steel under Periodic Stresses of Rectangular Wave
- Relaxation of 2^1/4 Cr-1 Mo Steel
- Crystallographic Study of Yield Condition of Polycrystalline Metals : 2nd Report, hcp Metal
- X-Ray Study of Surface Residual Stress Produced in Fatigue Process of Annealed Metals
- Influence of Frequency of Stress Cycles on Fatigue at Elevated Temperatures
- Investigation on Dynamic Creep and Rupture of a Low Carbon Steel