Relaxation of 2^1/4 Cr-1 Mo Steel
スポンサーリンク
概要
- 論文の詳細を見る
Relaxation, step down and creep tests were carried out on a Cr-Mo steel at a temperature of 500℃ and the characteristics of the material obtained by these tests are discussed in order to correlate them to each other. It was found that the log-log plot of stress versus strain rate in relaxation lies on a broken straight line. It may be considered that the relaxation in the higher stress range corresponds to transient creep and that in the lower stress range to steady creep. This simple correspondence dose not always hold, because the stress decrease during relaxation is accompanied by creep recovery. The predictions of relaxation using the informations obtained from other sorts of tests, which have been proposed up to this time, are not always satisfactory due to the lack of consideration of relaxation characteristics. Using the method presented by the authors, which is based on the fundamental relation between stress and plastic strain rate, the residual stress can be satisfactorily predicted. It is also found that a step down test is effective for determining the relaxation properties of materials.
- 一般社団法人日本機械学会の論文
著者
-
Taira Shuji
Faculty Of Engineering Kyoto University
-
Yamaguchi Masaru
Kawasaki Iron And Steel Mfg. Co.
-
SUZUKI Fusayuki
Faculty of Engineering, Kyoto University
-
Suzuki Fusayuki
Faculty Of Engineering Kyoto University
-
Taira S.
Faculty of Engineering, Kyoto University
関連論文
- Thermal Fatigue and Cyclic Mechanical Strain Fatigue at Elevated Temperature of 18-8 Cb Stainless Steel and 2.25 Cr-1 Mo Steel
- X-Ray Investigation on the Residual Stress of Metallic Materials : On the Residual Stress in Carbon Steel Caused by Thermal Stress
- Study on Fatigue Fracture in Quench-Tempered Carbon Steel : 3rd Report, On Propagation Process of Fatigue Crack
- Study on Fatigue Fracture in Quench-Tempered Carbon Steel : 2nd Report, Observation of Fatigue Crack Initiation Process by X-ray Microbeam Technique
- Study on Fatigue Fracture in Quench-Tempered Carbon Steel : 1st Report, Optical-Microscopic Observation of Fatigue Crack Initiation Process
- Creep Rupture of Internally Pressurized Cylinders at Elevated Temperatures
- X-Ray Investigation on Fatigue of Polycrystalline Metals : On the Relation between Crystal Orientation and Deformation in fcc Crystal
- Crystallographic Study of Yield Condition of Polycrystalline Metals : 1st Report, bcc Metal
- An Energetic Consideration of Fatigue Mechanism of Metal under Mean Stress
- X-ray Investigation on the Fatigue Damage of Metals
- X-Ray Investigation on Fatigue Damage of Metals under Mean Stress : 2nd Report, Torsional Fatigue
- X-Ray Investigation on Fatigue Damage of Metals under Mean Stress : (1st Report, Plane Bending Fatigue)
- X-Ray Investigation on the Prediction of Fatigue Life : On the Changes in Half-Value Breadth of Carbon Steel under Varying Stress Amplitudes
- Thermal Fatigue under Pulsating Thermal Stress Cycling
- Effect of Stress Reduction of Secondary Creep of Mild Steel
- Residual Stresses Produced by Plastic Tension in Notched Plate Specimens and Fatigue Strength
- Influence of Rest in Stress Alternation on the Fatigue Properties of a Low Carbon Steel at Elevated Temperatures
- On the Residual Stresses Due to Alternating Stressing of Annealed Steels
- Fatigue and Dynamic Creep Properties of 13 Cr Steel at Elevated Temperature under Combined Stresses of Static Tension and Alternating Bending
- Dynamic Creep and Fatigue of 13 Chromium Steel at Elevated Temperature
- X-Ray Investigation on Fatigue Fracture of Notched Steel Specimen : Observation of Fatigue Phenomena of Annealed Low-Carbon Steel by X-Ray Microbeam Technique
- X-ray Investigation of Stress Measurement : On the Method of Measurement, the Effect of Radiation Area and Resolving Power
- Crystallographic Study of Yield Condition of Polycrystalline Metals : (3rd Report, Relation between Slip in Crystals and Yield Condition)
- Creep of Mild Steel under Periodic Stresses of Rectangular Wave : (III) Prediction of the Creep Deformation under Periodic Stresses
- Creep of Mild Steel under Periodic Stresses of Rectangular Wave : (II) Creep Deformation under Unsymmetrical Periodic Stress Waves
- Creep of Mild Steel under Periodic Stresses of Rectangular Wave
- Relaxation of 2^1/4 Cr-1 Mo Steel
- Crystallographic Study of Yield Condition of Polycrystalline Metals : 2nd Report, hcp Metal
- X-Ray Study of Surface Residual Stress Produced in Fatigue Process of Annealed Metals
- Influence of Frequency of Stress Cycles on Fatigue at Elevated Temperatures
- Investigation on Dynamic Creep and Rupture of a Low Carbon Steel