Li二次電池用正極材料Li_<1+X>Mn_<2-X>O_4の熱力学的安定性と電池特性
スポンサーリンク
概要
- 論文の詳細を見る
We investigated the relation between cathode performance and the thermodynamic stability of the spinel Li_<1+x>Mn_<2-x>O_4(x=0-0.1)as a cathode active material for lithium secondary battery. The Mn valence was controlled by annealing conditions or changing the Li content. The heats of dissolution of the samples were measured by the solution calorimetry method. The standard enthalpy of formation, Δ_fH°, and the enthalpy change of reaction, ΔH, were calculated from the heat of dissolution. Δ_fH° and ΔH decreased and Mn valence increased with increasing Li content or higher P_<O_2> annealing treatment, leading to a good cycle performance in spite of a moderate decrease of initial capacity.
- 2000-09-01
著者
関連論文
- 5V級Li二次電池正極活物質LiMn_Ni_O_4の合成条件による物性, 結晶構造と電極特性の関係
- スラリーを用いた泳動電着法によるBa_Sr_xTiO_3誘電膜の作製
- Li二次電池正極活物質Li_Ni_Co_O_yの物性, 結晶構造と電極特性の熱処理条件依存
- Li二次電池正極活物質LiMn_2O_4の物性, 電極特性における超音波処理の影響
- Ce置換,Bi-Si-O添加によるSr-Ce-Bi-Ta-Si-O系強誘電体の結晶構造と強誘電性の変化
- リチウム二次電池正極活物質Li_x (Mn, Co, Ni, M) 0_2 (M=Al, Ti, Fe) の物性, 結晶・電子構造, 熱力学的安定性と電池特性
- 泳動電着法によるPb-Zr-Ti-Nb-Si-O系強誘電体厚膜の作製
- Li二次電池正極材料斜方晶LiMn_M_xO_2(M=Mn,Co,Ni)の結晶・電子構造と電極特性
- Li二次電池正極材料斜方晶LiMn_M_xO_2(M=Mn, Co, Ni, Zn)のMEM/Rietveld解析及び第一原理計算による電子構造の検討
- Li二次電池正極活物質Li_xCo_Ni_Mn_O_の物性, 結晶構造と電極特性のLi組成依存