SiO_2-B_20_3-Al_20_3-Zr0_2-RO-R_2O系ガラスの分相
スポンサーリンク
概要
- 論文の詳細を見る
The phase separation of SiO_2-B_2O_3-Al_2O_3-ZrO_2-RO-R_2O glasses and the composition of resulting porous glasses were com-pared with those of conventional Vycor type porous glasses. Phase separation progressed by the nucleation: growth mechanism, pore diameter increased with 1/3 power of time. The rate of phase separation in a ZrO_2 containing glasses was smaller than that of Vycor type by factors of 1/10-1/100. The rate determining step was considered to be the viscous flow of net-work structural waits. Amounts of Al_2O_3 and ZrO_2 remaining in the SiO_2 skeleton increased with increasing temperature and time. The composition of Vycor type porous glasses remained almost constant regardless of the heating conditions.
- 社団法人日本セラミックス協会の論文
- 1990-10-01
著者
-
森本 繁樹
セントラル硝子(株)硝子研究所
-
森本 繁樹
School Of Ceramic Engineering Institute Of Engineering Suranaree University Of Technology
関連論文
- 低融点リン酸塩ガラスの構造と性質に対するSiO_2の影響
- Te及びBi含有ガラスと結晶化ガラスの発光特性
- 分科会から見たガラスの製造と機能化研究への課題
- 溶出処理中の多孔質ガラスの割れ
- SiO_2-Al_2O_3-MgO-CaO-Na_2O系ガラスの結晶化に及ぼすTiO_2,ZrO_2及びP_2O_5の影響
- 多成分リン酸塩ガラスの性質に及ぼす1価及び2価イオンの影響
- フォトクロミックガラスの作製
- Li_2O-SiO_2系ガラスの結晶化に及ぼすK_2Oの効果
- ポーラスガラス中のKNO_3結晶の融点降下と相転移
- ハロゲン化銀を含むアルミノホウリン酸塩ガラスにおけるフォトクロミズム
- ハロゲン化銀フォトクロミックガラスの組成について : 極端に退色の遅いガラス
- ハロゲン化銀を含むアルミノホウケイ酸塩フォトクロミックガラスにおける各種酸化物の影響
- ハロゲン化銀を含むアルミノホウケイ酸塩ガラスにおけるフォトクロミック特性のガラス組成依存性
- フォトクロミック特性に対するガラス組成の影響
- イオン交換法によるLi_2O・2SiO_2系透明結晶化ガラスの強化
- Li_2O-SiO_2系透明結晶化ガラス中でのCr^イオンの生成と光吸収及び発光スペクトル
- Li_2O-SiO_2系透明結晶化ガラスの強度
- クローム含有透明結晶化ガラスの光吸収
- 住環境にやさしいガラス材料
- 高化学的耐久性ポーラスガラスの作製
- SiO_2-B_20_3-Al_20_3-Zr0_2-RO-R_2O系ガラスの分相
- SiO_2-AlPO_4系ポーラスガラスセラミックスの調製
- Na_2O-ZrO_2-P_2O_5-SiO_2系結晶化ガラスの電気伝導(イオン伝導性セラミックス)(伝導性セラミックス)