チタン酸アルミニウムの高温水蒸気腐食性

概要

論文の詳細を見る
Water vapor corrosion resistance of titanium aluminate (Al_2TiO_5) was examined at 1500℃ in 30 wt% H_2O flow. The weight loss rate of this substance was 8.6×10^<-6> g/cm^2・h during a 100-h test. No phase change occurred during the corrosion test, but anisotropic corrosion behavior was observed. In the X-ray diffraction patterns of the sample surface following the corrosion test, the relative intensities of 230 and 420 peaks were drastically decreased compared with that of the sample prior to corrosion. Geometrical patterns as like to sand ripples or terraced fields were obseirved on the sample surface after testing corresponding to the anisotropic water vapor corrosion. [Received June 5, 2003; Accepted August 29, 2003]
社団法人日本セラミックス協会の論文
2003-11-01