Stability and proton conductivity of AlH_2P_3O_<10>・nH_2O (n = 2-3) were investigated in the temperature range from 75℃ to 150℃ under various water vapor pressures. The hydrolysis from AlH_2P_3O_<10>・nH_2O to Al(H_2PO_4)_3 started at 100℃ under a relative humidity (RH) of 60%, and further hydrolysis to AlPO_4 took place with increasing temperature and humidity. At 75℃, the original phase was maintained under saturated water vapor pressure. Conductivity measurements at 75℃ (0%≦RH≦98%) and 100℃ (0%≦RH<60%) indicated an abrupt increase in conductivity with increasing water content n in the range of n = 1.0 to 2.0 at both temperatures. The proton conductivity achieved a value σ = 5.0 × 10^<-3>S・cm^<-1> at 75℃ and 98% RH. It is assumed that the proton conductivity in the crystal became larger by formation of continuous hydrogen-bonding in AlH_2P_3O_<10>・nH_2O.
- 社団法人日本セラミックス協会の論文
- 2003-05-01
著者
関連論文
- 新規交代層強誘電体Bi_2WO_6-Bi_3TaTiO_9
- 種々の外部水蒸気圧下におけるAlH_2P_3O_・nH_2Oの安定性とプロトン伝導特性
- 酸化タングステン水和物のプロトン伝導性 : 電気自動車用中温動作燃料電池の開発を目指して (材料界面マイクロ工学)
- a,b軸配向エピタキシャルBi_4Ti_3O_12基薄膜の合成と特性評価
- 欠陥制御によるチタン酸ビスマス多結晶体の高分極特性
- NOxを吸着したLa_,Ba_xSrCu_2O_の表面化学結合状態
- 中温作動燃料電池用プロトン伝導体の開発--金属酸化物水和物のプロトン導電性 (特集 水素製造と応用の最新動向(2))
- ポジトロニウム消滅寿命によるエポキシ樹脂中の自由体積空孔の可塑効果
- KrFエキシマレーザー照射によるSrTiO_3基セラミックス表面でのバリスター層の形成
- 回転塗布法によるWO_3系エレクトロクロミック膜の構造と特性
- 新奇メソ構造材料(バナジン酸-ポリエチレングリコール複合体)の設計
- バナジウム酸化物ゾルの光によるキャラクタリゼーション : 新型リチウム電池の開発を目指して ( 材料界面マイクロ工学)
- Pb,Co同時置換Bi_2VO_単結晶におけるイオン導電率
- 水和ジルコニア及び水和酸化スズのプロトン伝導性 (材料界面マイクロ工学)
- 学術講演「マイクロ・ナノ理工学」
- La置換および空孔導入によるSrBi_2Ta_2O_9の低抗電界化 : Defect Engineering による分極特性制御
- X線回折法による非晶質三酸化タングステン薄膜の骨格構造の評価
- Pb置換SrBi_2Ta_2O_9の格子ひずみと強誘電特性
- 強誘電体メモリー材料における格子欠陥と機能
- ビスマス層状構造酸化物の格子歪みと強誘電物性 ( 材料界面マイクロ工学)