Effects of attrition, prior acid-etching, and cyclic loading on the bond strength of a self-etching adhesive system to dentin
スポンサーリンク
概要
- 論文の詳細を見る
The purpose of this study was to evaluate the effects of dentin attrition, phosphoric acid etching, and cyclic loading on the microtensile bond strength (μTBS) of a self-etching adhesive system to dentin. Flat dentin surfaces of human molars were assigned to eight experimental groups based on those with or without attrition, prior acid-etching, and cyclic loading. Resin composite paste was placed and polymerized after the bonding procedure according to manufacturers instructions. The specimens were subjected to μTBS testing at a crosshead speed of 0.5 mm/min. Results showed that the minimum mean value of μTBS was 14.9 MPa in the group without attrition and acid-etching but with loading, while the maximum mean value of μTBS was 40.0 MPa in the group without attrition and loading but with acid etching. Therefore, the value of μTBS to dentin without attrition was significantly decreased by cyclic loading but that to dentin with attrition was not affected.
- 日本歯科理工学会の論文
- 2009-03-01
著者
-
KATOH Yoshiroh
Department of Operative Dentistry, School of Life Dentistry at Niigata, The Nippon Dental University
-
SUZUKI Masaya
Department of Operative Dentistry, School of Life Dentistry at Niigata, The Nippon Dental University
-
SHINKAI Koichi
Department of Operative Dentistry, School of Life Dentistry at Niigata, The Nippon Dental University
-
SUZUKI Shiro
Department of Prosthodontics, University of Alabama at Birmingham, School of Dentistry
-
Ebihara Takashi
日本歯科大学新潟生命歯学部 歯科保存学
-
Ebihara Takashi
Nippon Dental Univ. Niigata Hospital Niigata Jpn
-
Katoh Y
Department Of Operative Dentistry School Of Life Dentistry At Niigata The Nippon Dental University
-
Katoh Yoshiroh
日本歯科大学新潟病院 矯正歯科
-
Katoh Yoshiroh
Department Of Operative Dentistry The Nippon Dental University School Of Dentistry At Niigata
-
Katoh Yoshiroh
Department Of Operative Dentistry School Of Dentistry At Niigata The Nippon Dental University
-
Ebihara Takashi
Division Of Comprehensive Dentistry The Nippon Dental University Niigata Hospital
-
Suzuki Shiro
Department Of Prosthodontics University Of Alabama At Birmingham School Of Dentistry
-
Suzuki Shiro
Department Of Gastroenterology And Hepatology Tokyo Medical University
-
Shinkai Koichi
Department Of Operative Dentistry School Of Life Dentistry At Niigata The Nippon Dental University
-
Shinkai Koichi
Department Of Operative Dentistry The Nippon Dental University School Of Dentistry At Niigata
-
Shinkai Koichi
Department Of Operative Dentistry School Of Dentistry At Niigata The Nippon Dental University
-
Shirono Manabu
Division Of Comprehensive Dentistry The Nippon Dental University Niigata Hospital
-
WAKAKI Suguru
Division of Comprehensive Dentistry, The Nippon Dental University Niigata Hospital
-
SEKI Hideaki
Division of Comprehensive Dentistry, The Nippon Dental University Niigata Hospital
-
Suzuki Shiro
Materials Science & Advanced Devices Nhk Science & Technical Research Laboratories
-
Suzuki Shiro
鹿児島大学 医歯学総合研究科咬合機能補綴学
-
Seki Hideaki
Division Of Comprehensive Dentistry The Nippon Dental University Niigata Hospital
-
Wakaki Suguru
Division Of Comprehensive Dentistry The Nippon Dental University Niigata Hospital
-
Suzuki Masaya
Department Of Operative Dentistry School Of Life Dentistry At Niigata The Nippon Dental University
-
Suzuki Masaya
Department Of Electrical And Electronic Engineering Faculty Of Engineering And Resource Science Akit
-
Suzuki Masaya
Department Of Crop Physiology Faculty Of Agriculture Hokkaido University
-
SUZUKI Shiro
Department of Prosthodontics, School of Dentistry, University of Alabama at Birmingham
関連論文
- Observation of calcium phosphate powder mixed with an adhesive monomer experimentally developed for direct pulp capping and as a bonding agent
- Effect of fiber-premixed indirect resin composite substructure on fracture resistance of MOD composite inlays adhered with two different adhesive resin cements
- Effects of metal primers on bonding of adhesive resin cement to noble alloys for porcelain fusing
- Influence of Mechanical Properties of Two Resin Cements on Durability of Bond Strength to Dentin after Cyclic Loading
- A Novel Primer on Dentin Bonding of 4-META/MMA-TBB to Collagen-depleted Dentin
- Adhesion of 4-META/MMA-TBB Resin to Collagen-depleted Dentin : Effect of Conditioner with Ascorbic Acid/Ferric Chloride
- Effects of metal primers on bonding of adhesive resin cement to noble alloys for porcelain fusing
- Hard X-ray Detector (HXD) on board Suzaku
- Effect of Bonding Variables on the Shear Bond Strength and Interfacial Micromorphology of Prime & Bond/Dyract AP
- In-orbit performance of the hard X-ray detector on board Suzaku
- Dentin bond strength of a new adhesive system containing calcium phosphate experimentally developed for direct pulp capping
- Effects of attrition, prior acid-etching, and cyclic loading on the bond strength of a self-etching adhesive system to dentin
- In Vitro Evaluation of Bond Strength and Surface Roughness of a Resin-Paint Material
- Effect of the concentrations of calcium chloride and synthetic peptides in primers on dentin bond strength of an experimental adhesive system
- Response of CdZnTe Detectors on the Swift Burst Alert Telescope(Poster)
- Construction and Performance of a Large-Aperture Wire-Chamber Spectrometer for Pion Scattering Experiments at KEK
- Cytotoxicity of Dental Resin Monomers in the Presence of S9 mix Enzymes
- A Test of Lead Glass Shower Counters
- PIK3CA mutation and amplification in human lung cancer
- Simultaneous imaging of membrane antigen and the corresponding chromosomal locus in pathology archives
- Effects of moisture conditions of dental enamel surface on bond strength of brackets bonded with moisture-insensitive primer adhesive system
- Effect of light intensity for adhesives on shear bond strength to dentin
- Effect of Air-blowing Variables on Bond Strength of All-in-one Adhesives to Bovine Dentin
- Effect of filler size on wear resistance of resin cement
- Decrease in accumulation of ultrasound contrast microbubbles in non-alcoholic steatohepatitis
- Dynamic US contrast study of the liver : Vascular and delayed parenchymal phase
- Usefulness of contrast-enhanced ultrasonography with a new contrast mode, Agent Detection Imaging, in evaluating therapeutic response in hepatocellular carcinoma treated with radio-frequency ablation therapy
- Differential diagnosis of hepatic nodules using delayed parenchymal phase imaging of levovist contrast ultrasound : comparative study with SPIO-MRI
- A study of self-adhesive resin cements for bonding to silver-palladium-copper-gold alloy — Effect of including primer components in cement base
- Photoconductive Properties of Organic Films Based on Porphine Complex Evaluated with Image Pickup Tubes
- Ultra-High-Sensitivity New Super-HARP Pickup Tube and Its Camera(Recent Progress in Photon Detection Technology)
- Image Pickup from Zinc Phthalocyanine/Bathocuproine Double-Layer Film Using Pickup Tube
- Ultrahigh-Sensitivity Pickup Tube Using 35-μm-Thick HARP Photoconductive Film
- Effect of the concentrations of calcium chloride synthetic and peptides in primers on dentin bond strength of an experimental adhesive system
- Evaluation of Wear and Subsequent Dye Penetration of Endodontic Temporary Restorative Materials
- Evaluation of Temporary Restorative Materials for Endodontic Treatments
- Production of Monochromatic γ Rays from Thin Crystal of Silicon
- Numerical Simulation of Sand Erosion Phenomena in a Single-Stage Axial Compressor
- Chromosomal numerical abnormalities in early stage lung adenocarcinoma
- Improvement of Bonding to Bleached Bovine Tooth Surfaces by Ascorbic Acid Treatment
- Stained Margins of a 5-Year Old Composite Restoration : A Clinical and SEM Evaluation
- Stained Margins of a S-year old Composite Restoration: A Clinical and SEM Examination
- Monochromatization of Collimated Coherent Bremsstrahlung from a Thin Silicon Crystal
- Copy number estimation algorithms and fluorescence in situ hybridization to describe copy number alterations in human tumors
- Crystal Structure of Methyl 5-Acetamido-2-t-butyl-2-methyl-1,3-benzodioxole-4-carboxylate
- Study of dE/dx in a Drift Chamber with He-C_2H_6 Gas Mixture
- A study of self-adhesive resin cements for bonding to silver-palladium-copper-gold alloy-Effect of including primer components in cement base
- Identification and characterization of cancer stem cells in ovarian yolk sac tumors
- Newly Developed Diamond Points for Conservative Operative Procedures
- A Major Soybean QTL, qPDH1, Controls Pod Dehiscence without Marked Morphological Change
- Examination of T/CP Invariance in the e^+e^-τ^+τ^- Reaction
- Effect of CO_2 laser irradiation on wound healing of exposed rat pulp
- Dentin bond strength of an experimental adhesive system containing calcium chloride, synthetic peptides derived from dentin matrix protein 1 (pA and pB), and hydroxyapatite for direct pulp capping and as a bonding agent
- Histopathological and immunohistochemical study on the effects of a direct pulp capping experimentally developed adhesive resin system containing reparative dentin-promoting agents
- Direct pulp capping effect with experimentally developed adhesive resin systems containing reparative dentin-promoting agents on rat pulp : mixed amounts of additives and their effect on wound healing
- Shear bond strength of rebonded brackets after removal of adhesives with Er,Cr:YSGG laser
- RADIOPHARMACOLOGICAL STUDIES ON THE CADMIUM POISONING
- Clinical Evaluation of Intramuscular Administration of Natural Interferon-γ in the Treatment of Chronic Hepatitis B
- Mapping and use of QTLs controlling pod dehiscence in soybean
- Association between neuropeptide Y receptor 2 polymorphism and the smoking behavior of elderly Japanese
- Conditioning effects of cavities prepared with an Er,Cr:YSGG laser and an air-turbine
- EXPERIMENTAL STUDIES ON THE CARBONIC ANHYDRASE ACTIVITY IX. THE MODE OF ACTION OF ADRENOCORTICAL STEROIDS, ESPECIALLY ALDOSTERONE, ON THE CARBONIC ANHYDRASE IN MICE AND RATS
- BASAL STUDY ON EARLY DIAGNOSIS OF CADMIUM POISONING : CHANGE IN CARBONIC ANHYDRASE ACTIVITY
- Response of CdZnTe Detectors on the Swift Burst Alert Telescope(Poster)
- Effect of adherend temperature on bond strengths of resin bonding systems to denture base resin and a semi-precious alloy
- Effect of adhesion promoting monomer addition to MMA-TBBO resin on bonding to pure palladium
- Evaluation of fracture resistance of indirect composite resin crowns by cyclic impact test: Influence of crown and abutment materials
- Disintegration of sulfonated poly(1,4-piperazinediylterephthaloyl) microcapsules by 1-dodecylpyridinium chloride.
- Cell growth-inhibitory action of SAGP, an antitumor glycoprotein from Streptococcus pyogenes (Su strain).
- Effect of adhesion promoting monomer addition to MMA-TBBO resin on bonding to pure palladium
- Evaluation of fracture resistance of indirect composite resin crowns by cyclic impact test : Influence of crown and abutment materials
- Effect of adherend temperature on bond strengths of resin bonding systems to denture base resin and a semi-precious alloy