Adhesion of 4-META/MMA-TBB Resin to Collagen-depleted Dentin : Effect of Conditioner with Ascorbic Acid/Ferric Chloride
スポンサーリンク
概要
- 論文の詳細を見る
The purpose of this study was to evaluate ascorbic acid (AS) and ferric chloride (FE) for bonding 4-META/MMA-TBB resin to dentin that had been treated with NaClO. An experimental dentin conditioner consisting of 10%AS and 5%Fe (10AS-5FE) and three controls (10AS-OFE, 0AS-5FE, and 0AS-0FE) were prepared. Ascorcic acid neutralizes NaClO. The flattened dentin surfaces were modified sequentially with phosphoric acid etchant, NaClO agent, and the experimental conditioner, then each surface was bonded to a stainless steel rod with 4-META/MMA-TBB resin. The Super-Bond C&B (10-3/SB) system was also used. 24-hour tensile bond strengths were determined. The bonding system using 10AS-5FE conditioner showed significantly high bond strength compared to 10AS-0FE, 0AS-5FE, and 0AS-0FE. No significant differences were observed between 10AS-5FE and 10-3/SB. Microphotographs suggested that no hybrid layer formed in the 10AS-5FE group. Although the use of phosphoric acid and NaClO resulted in decreased bond strength between 4-META/MMA-TBB resin and dentin, additional conditioning with ascorbic acid and ferric chloride improved the bond strength.
- 日本歯科理工学会の論文
著者
-
Taira Yohsuke
Department Of Applied Prosthodontics Graduate School Of Biomedical Sciences Nagasaki University
-
Taira Yohsuke
Division Of Applied Prosthodontics Graduate School Of Biomedical Sciences Nagasaki University
-
Taira Y
Nagasaki Univ. Nagasaki Jpn
-
Taira Yohsuke
長崎大学 医歯薬学総合研究科健美補綴学
-
Taira Yohsuke
長崎大学 医歯薬学総合研究科摂食機能回復診断治療学
-
Taira Yohsuke
Nagasaki University Graduate School Of Biomedical Sciences Course Of Medical And Dental Sciences Dep
-
Taira Yohsuke
Division Of Fixed Prosthodontics And Oral Rehabilitation Nagasaki University Graduate School Of Biom
-
SOENO Kohyoh
Nagasaki University, Graduate School of Biomedical Sciences, Course of Medical and Dental Sciences,
-
SUZUKI Shiro
University of Alabama School of Dentistry, Department of Prosthodontics and Biomaterials, UAB School
-
ATSUTA Mitsuru
Nagasaki University, Graduate School of Biomedical Sciences, Course of Medical and Dental Sciences,
-
MATSUMURA Hideo
Nagasaki University, Graduate School of Biomedical Sciences, Course of Medical and Dental Sciences,
-
Taira Yohsuke
Division Of Fixed Prosthodontics And Oral Rehabilitation Nagasaki University Graduate School Of Biom
-
Soeno Kohyoh
Nagasaki University Graduate School Of Biomedical Sciences Course Of Medical And Dental Sciences Dep
-
Suzuki Shiro
Department Of Prosthodontics University Of Alabama At Birmingham School Of Dentistry
-
Suzuki Shiro
Materials Science & Advanced Devices Nhk Science & Technical Research Laboratories
-
Matsumura Hideo
Nagasaki University Graduate School Of Biomedical Sciences Course Of Medical And Dental Sciences Dep
-
Suzuki Shiro
鹿児島大学 医歯学総合研究科咬合機能補綴学
関連論文
- Shear Bond Strengths of Four Resin Bonding Systems to Two Silica-based Machinable Ceramic Materials
- Effect of fiber-premixed indirect resin composite substructure on fracture resistance of MOD composite inlays adhered with two different adhesive resin cements
- Bond Strength between Four Luting Systems and Enamel Modified with Phosphoric Acid
- Influence of Mechanical Properties of Two Resin Cements on Durability of Bond Strength to Dentin after Cyclic Loading
- Influence of Acid-base Conditioning on the Bond Strength of Five Luting Agents Employing Self-etching Primer to Enamel and Dentin
- A Novel Primer on Dentin Bonding of 4-META/MMA-TBB to Collagen-depleted Dentin
- Adhesion of 4-META/MMA-TBB Resin to Collagen-depleted Dentin : Effect of Conditioner with Ascorbic Acid/Ferric Chloride
- Effects of metal primers on bonding of adhesive resin cement to noble alloys for porcelain fusing
- Dentin bond strength of a new adhesive system containing calcium phosphate experimentally developed for direct pulp capping
- Effects of attrition, prior acid-etching, and cyclic loading on the bond strength of a self-etching adhesive system to dentin
- In Vitro Evaluation of Bond Strength and Surface Roughness of a Resin-Paint Material
- Comparison of Four Fluoride Etchants in Bonding between Titanium and a Self-curing Luting Agent
- Effect of Ceramic Coating by Aerosol Deposition on Abrasion Resistance of a Resin Composite Material
- The effect of magnesium oxide supplementation to aluminum oxide slip on the jointing of aluminum oxide bars
- Bond strength between luting materials and a fiber-reinforced resin composite for indirect restorations.
- The Physical Properties of a Machinable Resin Composite for Esthetic Restorations
- Effect of light intensity for adhesives on shear bond strength to dentin
- Effect of Air-blowing Variables on Bond Strength of All-in-one Adhesives to Bovine Dentin
- Effect of filler size on wear resistance of resin cement
- Effects of Primers Containing Thiouracil and Phosphate Monomers on Bonding of Resin to Ag-Pd-Au Alloy
- Effect of Four Silane Coupling Agents on Bonding of Two Resin-modified Glass Ionomer Cements to a Machinable Ceramic
- Photoconductive Properties of Organic Films Based on Porphine Complex Evaluated with Image Pickup Tubes
- Ultra-High-Sensitivity New Super-HARP Pickup Tube and Its Camera(Recent Progress in Photon Detection Technology)
- Image Pickup from Zinc Phthalocyanine/Bathocuproine Double-Layer Film Using Pickup Tube
- Ultrahigh-Sensitivity Pickup Tube Using 35-μm-Thick HARP Photoconductive Film
- Effect of the concentrations of calcium chloride synthetic and peptides in primers on dentin bond strength of an experimental adhesive system
- Evaluation of Wear and Subsequent Dye Penetration of Endodontic Temporary Restorative Materials
- Evaluation of Temporary Restorative Materials for Endodontic Treatments
- Improvement of Bonding to Bleached Bovine Tooth Surfaces by Ascorbic Acid Treatment
- A study of self-adhesive resin cements for bonding to silver-palladium-copper-gold alloy-Effect of including primer components in cement base
- Dentin bond strength of an experimental adhesive system containing calcium chloride, synthetic peptides derived from dentin matrix protein 1 (pA and pB), and hydroxyapatite for direct pulp capping and as a bonding agent
- Silane primers rather than heat treatment contribute to adhesive bonding between tri-n-butylborane resin and a machinable leucite-reinforced ceramic
- Effect of experimental acid/base conditioner on microtensile bond strength of 4-META/MMA-TBB resin to dentin after long-term water immersion
- Effects of sandblasting, H2SO4/HCl etching, and phosphate primer application on bond strength of veneering resin composite to commercially pure titanium grade 4
- Comparative study between laser sintering and casting for retention of resin composite veneers to cobalt-chromium alloy
- Thickness and surface structure of a ceramic layer created on three indirect resin composites with aerosol deposition
- Comparison of four silane primers and an isocyanate primer for bonding of tri-n-butylborane resin to a leucite-reinforced glass ceramic
- Effects of sandblasting, H_2SO_4/HCl etching, and phosphate primer application on bond strength of veneering resin composite to commercially pure titanium grade 4
- Effects of a fluoride etchant and a phosphate primer on bonding of veneering composite to Ti–6Al–4V alloy for CAD/CAM restorations
- Comparative study between laser sintering and casting for retention of resin composite veneers to cobalt-chromium alloy