Effects of Primers Containing Thiouracil and Phosphate Monomers on Bonding of Resin to Ag-Pd-Au Alloy
スポンサーリンク
概要
- 論文の詳細を見る
The purpose of the present study was to evaluate the effects of four experilnental prinlers on bond strength between a self-curing luting agent and silver-palladiuln-gold alloy. The experinlental primers were in lnixed solutions of a thiouracil primer (Metaltite) and a phosphate primer (Epricord, PM, PE, or PP), which were designated as Metaltite/Epricord,Metaltite/PM, Metaltite/PE, and Metaltite/PP respectively. Three prilners (Metal Primer II, V-Primer, and Alloy Primer) were also prepared as controls. Allunina-blasted metal alloys 'were bonded with acrylic rods. After 5,000 thermocycles, the maximu111 shear bond strength was obtained with Metaltite/PE (27.8±2.4 MPa) and Metaltite/Epricord (27.6± 5.9 MPa), followed by Metaltite/PP, Alloy Prilner, Metaltite, Metaltite/PM, Metal Primer II, V-Primer, and Epricord. PE, PM, and PP showed the lowest bond strength. Results of this study revealed that the cOlnbined use of a thiouracil Inonomer and a phosphate lnonomer ilnproved adhesive bonding. In this light, clinicians should pay attention to the types of functional monomers dissolved in a primer when fabricating resin-bonded prostheses.
- 日本歯科理工学会の論文
著者
-
ATSUTA Mitsuru
Division of Fixed Prosthodontics and Oral Rehabilitation, Nagasaki University Graduate School of Bio
-
Taira Yohsuke
Department Of Applied Prosthodontics Graduate School Of Biomedical Sciences Nagasaki University
-
Taira Yohsuke
Division Of Applied Prosthodontics Graduate School Of Biomedical Sciences Nagasaki University
-
Taira Y
Nagasaki Univ. Nagasaki Jpn
-
Taira Yohsuke
長崎大学 医歯薬学総合研究科健美補綴学
-
Taira Yohsuke
長崎大学 医歯薬学総合研究科摂食機能回復診断治療学
-
Taira Yohsuke
Nagasaki University Graduate School Of Biomedical Sciences Course Of Medical And Dental Sciences Dep
-
Taira Yohsuke
Division Of Fixed Prosthodontics And Oral Rehabilitation Nagasaki University Graduate School Of Biom
-
Taira Yohsuke
Division Of Fixed Prosthodontics And Oral Rehabilitation Nagasaki University Graduate School Of Biom
-
KAMADA Kohji
Division of Fixed Prosthodontics and Oral Rehabilitation, Nagasaki University Graduate School of Bio
-
Kamada Kohji
Division Of Applied Prosthodontics Graduate School Of Biomedical Sciences Nagasaki University
-
Atsuta Mitsuru
Division Of Applied Prosthodontics Graduate School Of Biomedical Sciences Nagasaki University
関連論文
- Shear Bond Strengths of Four Resin Bonding Systems to Two Silica-based Machinable Ceramic Materials
- Effects of Monomer Composition and Original Filler Content on Filler Loading in the Resulting Centrifuged Composites
- Color Stability of Acrylic Resin Adhesives with Different Initiation Modes
- Bond Strength between Four Luting Systems and Enamel Modified with Phosphoric Acid
- Influence of Mechanical Properties of Two Resin Cements on Durability of Bond Strength to Dentin after Cyclic Loading
- Influence of Acid-base Conditioning on the Bond Strength of Five Luting Agents Employing Self-etching Primer to Enamel and Dentin
- A Novel Primer on Dentin Bonding of 4-META/MMA-TBB to Collagen-depleted Dentin
- Adhesion of 4-META/MMA-TBB Resin to Collagen-depleted Dentin : Effect of Conditioner with Ascorbic Acid/Ferric Chloride
- Depth of cure and hardness of an indirect composite polymerized with three laboratory curing units
- A New Laboratory Polymerizing Apparatus Equipped with Halogen and Metal Halide Light Sources
- Effect of noble metal adhesive systems on bonding between an indirect composite material and a gold alloy
- A Nine-year Follow-up of a Porcelain Laminate Veneer Restoration Applied to an Adolescent with Traumatized Dentition : A Clinical Report
- Influence of Centrifugal Force on Filler Loading of Resin Composites
- Twenty-four Hour Bond Strength Between Layers of a Highly Loaded Indirect Composite
- Effectiveness of Bonding Systems on Bonding Durability of a Prefabricated Porcelain Material
- Comparison of Four Fluoride Etchants in Bonding between Titanium and a Self-curing Luting Agent
- Effect of Ceramic Coating by Aerosol Deposition on Abrasion Resistance of a Resin Composite Material
- The effect of magnesium oxide supplementation to aluminum oxide slip on the jointing of aluminum oxide bars
- Bond strength between luting materials and a fiber-reinforced resin composite for indirect restorations.
- The Physical Properties of a Machinable Resin Composite for Esthetic Restorations
- Influence of Laboratory Light-curing Unit Variation on Properties of Prosthetic Composites
- Effects of Primers Containing Thiouracil and Phosphate Monomers on Bonding of Resin to Ag-Pd-Au Alloy
- Effect of Four Silane Coupling Agents on Bonding of Two Resin-modified Glass Ionomer Cements to a Machinable Ceramic
- Influence of Light Irradiation Condition on Microshear Bond Strength of Dual-cured Resin Luting Agents
- Hardness Development of Dual-cured Resin Cements through Different Thicknesses of Ceramics
- Effects of Alumina-blasting and Adhesive Primers on Bonding between Resin Luting Agent and Zirconia Ceramics
- Silane primers rather than heat treatment contribute to adhesive bonding between tri-n-butylborane resin and a machinable leucite-reinforced ceramic
- Effect of experimental acid/base conditioner on microtensile bond strength of 4-META/MMA-TBB resin to dentin after long-term water immersion
- Effects of sandblasting, H2SO4/HCl etching, and phosphate primer application on bond strength of veneering resin composite to commercially pure titanium grade 4
- Comparative study between laser sintering and casting for retention of resin composite veneers to cobalt-chromium alloy
- Thickness and surface structure of a ceramic layer created on three indirect resin composites with aerosol deposition
- Comparison of four silane primers and an isocyanate primer for bonding of tri-n-butylborane resin to a leucite-reinforced glass ceramic
- Effects of sandblasting, H_2SO_4/HCl etching, and phosphate primer application on bond strength of veneering resin composite to commercially pure titanium grade 4
- Effects of a fluoride etchant and a phosphate primer on bonding of veneering composite to Ti–6Al–4V alloy for CAD/CAM restorations
- Comparative study between laser sintering and casting for retention of resin composite veneers to cobalt-chromium alloy