低炭素鋼の溶接部に生成したフェライトプレートの3次元観察(相変態・材料組織)

概要

論文の詳細を見る
The early stages of the formation of acicular ferrite in a low carbon steel weld were studied by serial sectioning and computer-aided three dimensional (3D) visualization. The specimens were taken from the weld of low carbon steel, containing 0.08% C, 0.9% Si, 1.57% Mn and 0.032% O, and were austenitized and isothermally reacted at 600 and 570℃ for less than 10s. Very thin and long plates were formed initially and thickening occurred probably after lengthening was hampered due to impingement on prior austenite grain boundaries and/or pre-formed ferrite plates. Multi-variant ferrite plates were nucleated at inclusions and grew radially in the directions close to <110>_γ with habit planes near {111}_γ, thus forming a characteristic "Widmanstatten star" noted earlier in a medium carbon steel on polished surfaces.
社団法人日本鉄鋼協会の論文
2005-07-01