Hydrothermal Synthesis of Zeolite A Using Blast Furnace Slag
スポンサーリンク
概要
- 論文の詳細を見る
Alkali hydrothermal synthesis of zeolite A using blast furnace (BF) slag was investigated. The preliminary experiment was conducted in use of synthetic slag consisting of SiO2, Al2O3, and CaO powders, and it was made clear that the most optimum slag compositions to synthesize zeolite A were the molar ratio of Si to Al (Si/Al) of 1 and reduction of CaO content down to 15 mass%, and that hydrothermal treating conditions were the temperature range from 328 to 358 K, NaOH solution of 1 M (=mol/L) and the ratio of the volume of NaOH solution to total mass of slag (Vsol/Wslag) of 15 (mL/g). It was also found that synthetic slag with such a higher content of CaO as 40 % resulted in formation of tobermorite and hydrogarnet. In the experiment using BF slag, zeolite A could be successfully synthesized by optimizing both conditions of the compositions of raw material powders and hydrothermal treatment as noted above, where optimization of the compositions of raw material powders such as Si or Al content were performed by the suitable amount of addition of SiO2 powder or NaAlO2 powder as a source of Si and Al. The ball milling type reaction vessel containing numerous small SiC balls which was first adopted in this hydrothermal treating study was confirmed to be very effective for acceleration of synthetic reaction rate, shortening markedly the time period needed for fully synthesis of zeolite A. Temperature dependence of heat capacity of zeolite A powder synthesized in use of BF slag was measured after absorption of vapor at the ambient temperature, showing endothermic behavior with the peak at the temperature of around 473 K.
- 社団法人 日本鉄鋼協会の論文
- 2005-06-15
著者
-
井口 〓孝
Department Of Materials Processing Tohoku University
-
井口 泰孝
東北大学大学院工学研究科
-
MURAKAMI Taichi
Department of Materials Processing, Tohoku University
-
OUCHI Chiaki
Department of Materials Processing, Tohoku University
-
IGUCHI Yasutaka
Department of Metallurgy, Tohoku University
-
Murakami Taichi
Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
Ouchi C
Department Of Materials Processing Tohoku University
-
Ouchi Chiaki
Tohoku University
-
Murakami Taichi
Department Of Materials Processing Tohoku University
-
Murakami Taichi
Department Of Chemistry And Materials Science Tokyo Institute Of Technology
-
SAHARA Ryoji
Department of Materials Processing, Tohoku University
-
SUGANO Yoshiyuki
Department of Metallurgy, Faculty of Engineering, Tohoku University
-
SAHARA Ryouji
Institute for Materials Research, Tohoku University
-
NARUSHIMA Takayuki
Biomedical Engineering Research Organization, Tohoku University
-
Sugano Yoshiyuki
Department Of Metallurgy Faculty Of Engineering Tohoku University
-
Iguchi Yasutaka
Department Of Materials Processing Tohoku University
-
Sahara Ryouji
Department Of Materials Processing Tohoku University
-
Ouchi Chiaki
Department Of Metallurgy Tohoku University
-
Ouchi Chiaki
Department Of Materials Processing Graduate School Of Engineering Tohoku University
関連論文
- 110 高融点金属と溶鉄の混合熱測定(製鋼基礎・脱酸, 製鋼, 日本鉄鋼協会 第 95 回(春季)講演大会)
- 182 高融点金属と溶鉄の混合熱測定(熱力学・反応速度・脱炭, 製鋼, 日本鉄鋼協会第 92 回(秋季)講演大会)
- Surface Hardening Treatment for Titanium Materials Using Ar-5%CO Gas in Combination with Post Heat Treatment under Vacuum
- 機能的電気刺激用体内埋め込み電極の機械的・電気的特性と臨床評価
- ラマン分光法による CaO-MeO-SiO_2, MnO-SiO_2 および FeO-SiO_2 系スラグの構造研究
- 高炉スラグ中のガスの挙動
- ラマン分光法による珪酸塩スラグの構造解析
- 高温熱量計による鉄合金の混合熱の測定 : Fe-Cr, Fe-Mo, Fe-W, Fe-V, Fe-Nb, Fe-Ta
- 高温熱量計による鉄合金の混合熱の測定
- 108 ラマン分光法による MnO-SiO_2, FeO-SiO_2 および CaO-MeO-SiO_2 系スラグの構造研究(精錬基礎, 製鋼, 日本鉄鋼協会 第 101 回(春季)講演大会)
- 56 高炉スラグ中のガス成分の定量(製銑スラグ・製銑基礎 (II), 製銑, 日本鉄鋼協会 第 100 回(秋季)講演大会)
- 166 ラマン分光法による珪酸塩スラグの構造研究(製鋼基礎・造塊, 製鋼, 日本鉄鋼協会 第 98 回(秋季)講演大会)
- 東北大学工学部金属物理化学講座・研究紹介
- セルモデルによる溶融スラグのハイドロオキシルキャパシティーの定式化
- 溶融アルミネート中への水蒸気の溶解
- CO_2ガスを利用したチタンおよびチタン合金の表面硬化処理(加工・加工熱処理)
- TiB及びY_2O_3分散粒子による粉末冶金チタン合金のβ粒微細化
- Boron and Nitrogen in GaAs and InP Melts Equilibrated with B_2O_3 Flux
- Behavior of Oxygen in Ga-As Melts with the Range of As Content up to 5 mass % Equilibrated with B_2O_3 Flux
- Activity of Ga_2O_3 in B_2O_3 Flux and Standard Free Energies of Formation of CaBO_3 and InBO_3
- 111 溶融スラグを介したガス相からの溶鉄への水素移行(製鋼基礎・脱酸, 製鋼, 日本鉄鋼協会 第 95 回(春季)講演大会)
- 134 スラグを通しての溶鉄への水素の溶解(反応速度・物性, 製鋼, 日本鉄鋼協会第 90 回(秋季)講演大会)
- 溶融 Fe_tO-SiO_2 系スラグの生成熱測定
- Dynamic and Static Restoration Behaviors of Pure Lead and Tin in the Ambient Temperature Range
- The Effect of Solute Elements on Hardness and Grain Size in Platinum Based Binary Alloys
- Hydrothermal Synthesis of Zeolite A Using Blast Furnace Slag
- Dissimilar Metal Joining of Aluminum to Steel by MIG Arc Brazing Using Flux Cored Wire
- Effect of Tool Plunging Downforce on Friction Stir Welding of ADC12 Die Cast Alloy(Physics, Processes, Instruments & Measurements, INTERNATIONAL SYMPOSIUM OF JWRI 30TH ANNIVERSARY)
- Dissimilar Metal Joining of Steel to Aluminum by Lap Joint MIG Arc Brazing(Physics, Processes, Instruments & Measurements, INTERNATIONAL SYMPOSIUM OF JWRI 30TH ANNIVERSARY)
- ラマン分光法を用いた高温酸化皮膜の"その場"観察装置の開発
- Mechanisms of Carburization and Melting of Iron by CO Gas
- Mechanism of Carburizing Followed by Melting of Iron by CO Gas
- チタン合金のβ粒微細化及び粒成長挙動に及ぼすY_2O_3分散粒子の影響
- 極微量のイットリウム添加α+β型チタン合金のβ粒成長に及ぼす加熱温度・時間の影響
- 鉄鋼スラグ及び結晶性Al_2O_3を原料としたゼオライトAのアルカリ水熱合成
- 鋳造低合金鋼での動的再結晶後のγ粒成長挙動に及ぼす微量元素の影響
- 動的再結晶による鋼の凝固オーステナイト粒の微細化及び粒成長挙動
- 析出粒子及び動的再結晶による凝固オーステナイト粒径の微細化
- 溶鉄のバリウムによる脱酸平衡
- 技術経営における知的財産戦略 : 企業資産としての知的財産を活用した経営戦略の重要性
- 情報化社会に伴う特許法のパラダイム・シフトと情報保護法としての新たな制度設計
- 発明概念の研究 (特集 大学における知的財産の研究)
- 高温熱量計によるニッケルおよびコバルト合金の混合熱測定
- 連続鋳造による9%Ni鋼のミクロ偏析に及ぼすオーステナイトでの動的再結晶の影響
- Fatigue Behaviors of Ultra Fine Wires of β-Type and α-Type Titanium Alloys
- Oxidation or Nitridation Behavior of Pure Chromium and Chromium Alloys Containing 10mass%Ni or Fe in Atmospheric Heating
- Alloy Design and Property Evaluation of New β Type Titanium Alloy with Excellent Cold Workability and Biocompatibility
- Preparation of Calcium Phosphate Films by Radiofrequency Magnetron Sputtering
- Grain Refinement of As Cast Austenite by Dynamic Recrystallization in HSLA Steels
- Solubilities and Equilibrium Distribution Coefficients of Oxygen and Carbon in Silicon
- 鉄鋼スラグを原料としたぜオライト類のアルカリ水熱合成
- Mechanisms of Pig-iron Making from Magnetite Ore Pellets Containing Coal at Low Temperature
- 溶融 CaO-SiO_2-MgO, CaO-SiO_2-TiO_2 系スラグにおける水蒸気溶解度および溶解速度
- シンポジウム : 次世代の工学教育と社会
- 技術経営人材育成
- 特集にあたって(東北支部特集)
- 東北支部シンポジウム「理科教育を考える」 : 新教育課程は現場ではどのように実践されているのか
- 産学官の連携強化 WG 報告
- 純酸素による溶融 Fe-Ni, Fe-Cr 合金の酸化速度
- 212 純酸素による溶融鉄-クロム, 鉄-ニッケル合金の酸化速度(反応速度・攪拌・混合・転炉・転炉スラグ, 製鋼, 日本鉄鋼協会 第 102 回(秋季)講演大会)
- 米国技術移転サイクルの提案と検証
- 産学連携Forum(第3回)米国大学TLOの技術移転発展モデルの提案と検証
- 1A10 米国技術移転発展モデルの提案とその検証(産学連携, 第20回年次学術大会講演要旨集I)
- 大学から見たベンチャー起業の必要性と将来展望
- 米国の大学における技術移転に関する研究
- 超微細組織を有する生体用新α+β型チタン合金の熱処理特性
- 133 溶融鉄および鉄-クロム合金の脱窒速度(インジェクション基礎, 反応速度, 製銑・製鋼共通, 日本鉄鋼協会第 109 回講演大会)
- Alloy Design and Properties of New α+β Titanium Alloy with Excellent Cold Workability, Superplasticity and Cytocompatibility
- Evaluation of Sliding Wear Resistant Property of C. P. Titanium and SP-700 Titanium Alloy Surface-hardened by Ar-5%CO Gas
- Variations in the Microstructure and Hardness with Solution Treating and Aging Conditions in New α+β Titanium Alloy Ti-4.5%Al-6%Nb-2%Fe-2%Mo
- β Grain Refinement due to Small Amounts of Yttrium Addition in α+β Type Titanium Alloy, SP-700
- ライム系物質の水和反応
- Surface Hardening Treatment for C.P. Titanium and Titanium Alloys in Use of Ar-5%CO Gas
- 討 6 還元性ガスによる溶融酸化鉄の還元反応速度(I 鉄鉱石類の高温における還元・溶融機構, 第 107 回 講演大会討論会講演概要)
- 溶解熱熱量計による製鋼スラグの水和熱測定
- 製鋼スラグの水和機構解明
- 高温熱量計の試作と予備実験; 銅合金系の混合熱の測定
- BaO-MgO-Al_2O_3におけるBaβ-アルミナの作製とその電気的性質測定
- Sr β-アルミナイオン伝導体の作製とそのa.c.インピーダンス測定
- 情報化社会に伴う特許法のパラダイム・シフト
- 143 製鋼温度における合金の混合熱測定(反応速度・脱酸・熱力学, 製鋼, 日本鉄鋼協会 第 86 回(秋季)講演大会)
- Alkali Hydrothermal Synthesis of Zeolite A Using Oxide By-products
- Oxidation of Boron Carbide-Silicon Carbide Composite at 1073 to 1773K
- (4) 溶融シリコン中の不純物元素の物理化学的挙動(主題 : 素材・材料プロセスに係わる物性と評価)(素材工学研究所第 6 回研究懇談会)(素材工学研究会記事)
- 太陽電池用シリコン製造プロセスにおける軽元素不純物の挙動に関する熱力学的研究
- 溶融 CaO-SiO_2-Al_2O_3 系スラグにおける水蒸気溶解度および溶解速度
- 279 溶融 CaO-SiO_2-Al_2O_3 系スラグの水蒸気溶解速度(溶鋼処理(II)・物性, 製鋼, 日本鉄鋼協会第 104 回(秋季)講演大会)
- 溶融 Cr および溶融 Cr-Fe 合金の窒素溶解度
- 溶融ガリウムおよび溶融インジウムの酸素溶解度
- 294 溶融クロムおよび溶融クロム・鉄合金の窒素溶解度(熱力学・起電力・反応速度, 製鋼, 日本鉄鋼協会 第 100 回(秋季)講演大会)
- Recovery of Calcium from BF Slag and Synthesis of Zeolite A Using Its Residue
- 2・2 高等学校の理数系教諭の製鉄所見学会と鉄鋼技術者、研究者との懇談会(2. 東北支部の事業, 東北支部から会員の皆様へ)(支部だより)
- エリオットシンポジュウム
- 日本の大学で Faculty Club は育つだろうか
- 溶融ウスタイトの CO による還元反応速度
- 溶融ウスタイトの水素による還元反応速度
- 110 溶融 Fe_tO-SiO_2, Fe_tO-CaO 及び Fe_tO-CaO-SiO_2 系スラグの CO による還元反応速度(還元, 石炭, 流動層, 製銑, 日本鉄鋼協会第 108 回(秋季)講演大会)
- 61 溶融ウスタイトの還元速度に及ぼす添加酸化物 (SiO_2, CaO, Al_2O_3, TiO_2) の影響(製銑基礎, 高炉 (4) システム・耐火物・コークス, 製銑, 日本鉄鋼協会第 107 回(春季)講演大会)
- 174 溶融酸化鉄の水素還元速度(製銑基礎, 製銑, 日本鉄鋼協会第 104 回(秋季)講演大会)
- 49 溶融ウスタイトの CO による還元反応速度(還元機構・還元鉄・高圧還元・スラグ (1), 製銑, 日本鉄鋼協会 第 106 回(秋季)講演大会)