Improvement in the Cumulative Failure Distribution of High-$k$ Dielectric Subjected to Nanoscale Stress by D2 Post-Deposition Annealing
スポンサーリンク
概要
- 論文の詳細を見る
By taking advantage of the small contact area of the conductive atomic force microscopy (CAFM) tip with the sample surface, and the powerful measurement capability of the semiconductor parameter analyzer, a nanoscale stress was applied to the atomic-layer-deposited (ALD) HfO2 high-$k$ dielectrics prepared with N2, D2, and no post-deposition anneal (PDA), respectively. The statistical breakdown behavior of ALD HfO2 under nanoscale stresses was determined and is presented in this paper. It is evident that the cumulative failure distribution of breakdown voltage of high-$k$ dielectrics under nanoscale CVS basically follows the Weibull statistics. We also found that the ALD HfO2 prepared with D2 PDA showed an obvious improvement in cumulative failure distribution when compared with those prepared with N2 PDA and no PDA. The result indicates that D2 PDA can substantially suppress the generation of defects during the application of nanoscale stress and improve the reliability of high-$k$ dielectrics.
- 2009-11-25
著者
-
Wu You-lin
Department Of Electrical Engineering National Chi-nan University
-
Liang Cheng-Hsun
Department of Electrical Engineering, National Chi Nan University, 1 University Rd., Nantou, Puli, Nantou, Taiwan 54561, R.O.C.
-
Huang Chiung-Yi
Department of Electrical Engineering, National Chi Nan University, 1 University Rd., Nantou, Puli, Nantou, Taiwan 54561, R.O.C.
-
Wu You-Lin
Department of Electrical Engineering, National Chi Nan University, 1 University Rd., Nantou, Puli, Nantou, Taiwan 54561, R.O.C.
関連論文
- Stress Reliability Comparison of Metal-Oxide-Semiconductor Devices with CoSi_2 and TiSi_2 Gate Electrode Materials
- Modeling Nanoscale Current Conduction in HfO2 High-$k$ Dielectrics
- Effect of Starting Oxide Preparation on Electrical Properties of Reoxidized Nitrided and N_2O-Annealed Gate Oxides
- Improvement in the Cumulative Failure Distribution of High-$k$ Dielectric Subjected to Nanoscale Stress by D2 Post-Deposition Annealing
- Novel Dry-Type Glucose Sensor Based on a Metal–Oxide–Semiconductor Capacitor Structure with Horseradish Peroxidase + Glucose Oxidase Catalyzing Layer