Structure and Electrical Studies of Fluorinated Amorphous Carbon Films Prepared by Electron Cyclotron Resonance/Chemical-Vapor Deposition
スポンサーリンク
概要
- 論文の詳細を見る
Fluorinated amorphous carbon (a-C:F) films of high fluorine content were prepared by radio-frequency (RF) bias assisted electron cyclotron resonance/chemical-vapor deposition (ECR-CVD) with a variable fluorine-to-carbon (F/C) ratio of the feed gases. The films were characterized by X-ray photoelectron spectroscopy (XPS), electron energy loss spectroscopy (EELS) and transmission electron microscopy (TEM). A low dielectric constant of around 1.5 and high dielectric strength beyond 35 MV/cm were obtained under the as-deposited and annealed conditions, respectively. The measured huge current surge and electrical conductivity of the films were discussed on the basis of the nanovoids and sp2/sp3 bonding fractions as derived from the above characterizations.
- Published by the Japan Society of Applied Physics through the Institute of Pure and Applied Physicsの論文
- 2003-06-15
著者
-
Shih Han
Department Of Material Science And Engineering National Tsing-hua University
-
Lin Pang
Department Of Materials Science And Engineering National Chiao Tung University
-
Huang Kun
Department of Materials Science and Engineering, National Chiao-Tung University, Hsinchu 300, Taiwan, Republic of China
関連論文
- The Microstructure of As Precipitates in Si Delta-Doped GaAs Grown by Low-Temperature Molecular Beam Epitaxy
- Effects of Metallo-Organic Decomposition Agents on Thermal Decomposition and Electrical Conductivity of Low-Temperature-Curing Silver Paste
- Selected-Area Growth of SnO_2 Nanowires on TiO_2 Layer through Reduction of Hydrogen Gas
- Accelerated Degradation of High Power Light-Emitting Diode Resulted from Inhomogeneous Current Distribution
- Synthesis of Tungsten Oxide Nanoslab Bundles by Microwave Plasma-Enhanced Chemical Vapor Deposition
- Self-Constraining Method for Low Shrinkage of Low-Temperature-Cofired Ceramic Devices
- Microstructure and Electrical Resistivity of Low-Temperature-Cured Silver Films Prepared Using Silver Oxide and Silver Stearate Pastes
- Variation of Electrostatic Discharge Robustness Induced by the Surface Morphology of High Power Light-Emitting Diodes
- High-Frequency Electrical Properties of Silver Thick Films Measured by Dielectric Resonator Method
- Sputter Deposition of Multi-Element Nanoparticles as Electrocatalysts for Methanol Oxidation
- Method of Estimating Dielectric Properties of Dielectric Layers in Low-Temperature-Cofired Ceramic Devices
- Effects of Silver Oxide Addition on the Electrical Resistivity and Microstructure of Low-Temperature-Curing Metallo-Organic Decomposition Silver Pastes
- Characterization of the Low-Curing-Temperature Silver Paste with Silver 2-Ethylhexanoate Addition
- Structure and Electrical Studies of Fluorinated Amorphous Carbon Films Prepared by Electron Cyclotron Resonance/Chemical-Vapor Deposition
- Sol–Gel-Derived Zn(1-x)MgxO Thin Films Used as Active Channel Layer of Thin-Film Transistors
- Characterization and Cathodoluminescence of Beak-Like SnO2 Nanorods
- Selected-Area Growth of SnO2 Nanowires on TiO2 Layer through Reduction of Hydrogen Gas